| Solidification Structure of Continuous Casting Large Round Billets under Mold Electromagnetic Stirring |
| Tao SUN1,2,Feng YUE1,2,Hua- jie WU1,2,Chun GUO1,2,Ying LI3,Zhong- cun MA3 |
1. Metallurgical Engineering Research Institute, University of Science and Technology Beijing, Beijing 100083, China
2. Collaborative Innovation Center of Steel Technology, University of Science and Technology Beijing,Beijing 100083, China
3. Beiman Special Steel Co. , Ltd. , Qiqihaer 161041, Heilongjiang, China |
|
|
|
|
Abstract The solidification structure of a continuous casting large round billet was analyzed by a cellular- automaton- finite- element coupling model using the ProCAST software. The actual and simulated solidification structures were compared under mold electromagnetic stirring (MEMS) conditions (current of 300 A and frequency of 3 Hz). Thereafter, the solidification structures of the large round billet were investigated under different superheats, casting speeds, and secondary cooling intensities. Finally, the effect of the MEMS current on the solidification structures was obtained under fixed superheat, casting speed, secondary cooling intensity, and MEMS frequency. The model accurately simulated the actual solidification structures of any steel, regardless of its size and the parameters used in the continuous casting process. The ratio of the central equiaxed grain zone was found to increase with decreasing superheat, increasing casting speed, decreasing secondary cooling intensity, and increasing MEMS current. The grain size obviously decreased with decreasing superheat and increasing MEMS current but was less sensitive to the casting speed and secondary cooling intensity.
|
|
Received: 21 May 2015
Published: 14 April 2016
|
|
Corresponding Authors:
Tao SUN
E-mail: suntaoking@126.com
|
|
|
|
| [1] |
Kang-wei LI , Chang-ling ZHUANG , Jian-hua LIU, Shao-bo SHEN , Yi-long JI, Zhi-biao HAN. Plasticity Steel for Automobiles[J]. Chinese Journal of Iron and Steel, 2015, 22(Supplement 1): 75-79. |
| [2] |
Ying-tie XU,Zhao-ping CHEN,Mao-tao GONG,,Da SHU,Yue-mei TIAN,,Xiang-qian YUAN. Effects of Mg Addition on Inclusions Formation and Resultant Solidification Structure Changes of Ti-stabilized Ultra-pure Ferritic Stainless Steel[J]. Chinese Journal of Iron and Steel, 2014, 21(6): 583-588. |
| [3] |
LI Qiu��shu;LI Hai��bin;ZHAI Qi��jie. Structure Evolution and Solidification Behavior of Austenitic Stainless Steel in Pulsed Magnetic Field[J]. Chinese Journal of Iron and Steel, 2006, 13(5): 0-69. |
|
|
|
|
2016, Vol. 23 