Evolution of Microstructure and Ordering in Rolling Process of Fe-6.5 mass% Si Alloy |
Hui LI,Yong-feng LIANG,Feng YE |
State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing 100083, China Fe-6.5 mass% Si alloy is an excellent soft magnetic material with good application prospects. After rolling, the structure of the sheet is likely to be heterogeneous along the normal direction. The microstructure and ordering evolution in the thickness range of the sheets during hot-warm rolling process was studied by means of optical microscope and transmission electron microscope. The results show that dynamic recrystallization occurs in the surface parts during the hot and warm rolling processes, where the grains are equiaxed but have high density of dislocations due to the large deformation. The grains in the center part are elongated along the rolling direction. It is also found that in the hot rolled sheet, the center part has lower density of dislocations because of dynamic recovery. Meanwhile, this part has higher ordering content compared with the surface part, indicating that the high density of dislocations can inhibit the formation of ordering in the air cooling process after hot rolling. In the warm rolling process, both of the parts are deformed heavily. Large deformation destroys ordered phases and induces disordering. The ordering content is low in the whole warm rolled sheet. |
|
|
Abstract rolling process; microstructure; ordering; Fe-6.5 mass% Si alloy
|
Received: 06 March 2015
Published: 06 May 2016
|
Fund:the Major State Basic Research Development Program of China;the High-tech Research and Development Program of China;the National Natural Science Foundation of China |
|
|
|
[1] |
Yang Yun,Qing-wu Cai,,Bao-sheng Xie,*,Shuang Li. Effect of tempering temperature on strain hardening exponent and flow stress curve of 1000 MPa grade steel for construction machinery[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 950-956. |
[2] |
Ying Ci,*,Zhan-zhan Zhang. Simulation study on heat-affected zone of high-strain X80 pipeline steel[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 966-973. |
[3] |
Xiao-li Zhao,,Yong-jian Zhang,Cheng-wei Shao,Wei-jun Hui,Han Dong. Thermal stability of retained austenite and mechanical properties of medium-Mn steel during tempering treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 830-837. |
[4] |
Hang-wei Zhou,,Hui-qun Liu,,Dan-qing Yi,,Yu Xiao,,Xiao-long Zhao,Jian Wang,Qi Gao. Effect of �� phase on fatigue crack growth of Ti-6242 alloy[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 811-822. |
[5] |
Qiu-lin Niu,,Wei-wei Ming,Ming Chen,Si-wen Tang,,Peng-nan Li,. Dynamic mechanical behavior of ultra-high strength steel 30CrMnSiNi2A at high strain rates and elevated temperatures[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 724-729. |
[6] |
Reng-chong Xu,,Yan-lin He,,Hu Jiang,,Hua Wang,,Na-qiong Zhu,,Xiao-gang Lu,, Lin Li,. Microstructures and mechanical properties of ferrite-based lightweight steel with different compositions[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 737-742. |
|
|
|
|