| Stretch Bending of Z-section Stainless Steel Profile |
| Zheng-wei GU1,2,Meng-meng L��1,2,Xin LI1,2,Hong XU1,2 |
1. State Key Laboratory of Automobile Materials, Jilin University, Changchun 130025, Jilin, China
2. Department of Materials Science and Engineering, Jilin University, Changchun 130025, Jilin, China |
|
|
|
|
Abstract The stretch bending properties of a new Z-section stainless steel profile were investigated by simulation. The causes of the forming defects, such as section distortions and poor contour precision, were analyzed, and the corresponding controlling methods were proposed. The results show that the main forming defects for the stretch bending of the Z-section profile were the flange sagging, the sidewall obliquing inward, the bottom surface upwarping, and the bad contour accuracy; the cross-section distortions were mainly induced by the shrinkage of the sidewall, which could be eliminated by increasing the sidewall height of the profile reasonably; the poor contour precision was mainly due to springback, which could be controlled by modifying the die surface based on the springback amount; for the investigated bending beam, the proper sidewall height compensation was 2 mm, and the suitable die surface modification amount was 1.2 times of the springback amount, when the elongation was 10% of the initial profile length. Stretch bending tests were conducted on a new type of die with adjustable bending surfaces, and high quality components were achieved, which verified the effectiveness of the defect controlling measures.
|
|
Received: 13 January 2016
Published: 12 June 2016
|
| Fund:Major Technology Program of Ministry of Industry and Information Technology of China;National Outstanding Youth Science Fund Project;Technology Development Program of Jilin Province |
|
Corresponding Authors:
Hong Xu
E-mail: xuhong20141011@163.com
|
|
|
|
| [1] |
Da-shan Sui,*,Hai-ming Zhang,Hong-yang Zhu,Zhe Zhu,Zhen-shan Cui. Effects of process parameters on fragment and refinement of millimeter-grade coarse grains for 316LN steel during hot cogging[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 529-535. |
| [2] |
Cun-jiang TANG,Shi-long LIU,Cheng-jia SHANG. Micromechanical Behavior and Failure Mechanism of F/B Multi-phase High Performance Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(5): 489-494. |
| [3] |
Yang LI,,An-yuan DENG,,Chuan-qi YIN,,Sai-juan ZHANG,,En-gang WANG,. Effects of Magnetic Pressure Constraint on Dynamic Deformation and Oscillation Behavior of Metal Free Surface[J]. Chinese Journal of Iron and Steel, 2016, 23(11): 1134-1141. |
| [4] |
Jian-an ZHOU, Kang WEI, Zhi-qiang LI , Zhong-qiu LIU , Xue-kai JIANG, Hong-wei NI. Numerical Simulation of Gas-powder Flow in a Slot-plug Mixing Chamber[J]. Chinese Journal of Iron and Steel, 2015, 22(Supplement 1): 24-29. |
| [5] |
Peng-huan LI, Qiao-jun WU, Wen-hao HU, Jian-song YE. Mathematical Simulation of Behavior of Carbon and Oxygen in RH Decarburization[J]. Chinese Journal of Iron and Steel, 2015, 22(Supplement 1): 63-67. |
| [6] |
Wen-jie WU , Hui-xiang YU, Xin-hua WANG, Hai-bo LI , Ke LIU. Optimization on Bottom Blowing System of a 210 t Converter[J]. Chinese Journal of Iron and Steel, 2015, 22(Supplement 1): 80-86. |
|
|
|
|
2016, Vol. 23 