Mechanism and Improvement of Straight Edge Seam Defect on Hot-rolled Plate Surfaces through Use of Chamfered Slabs |
Hui ZHANG1,Peng HU1,2,Ming-lin WANG1 |
1. National Engineering and Research Center for Continuous Casting Technology, Central Iron and Steel Research Institute, Beijing 100081, China 2. School of Metallurgy, Northeastern University, Shenyang 110819, Liaoning, China |
|
|
Abstract To improve the straight edge seam defect on hot-rolled steel plates, the deformation and temperature distribution of rectangular slabs and chamfered slabs during rolling in a pilot rolling experiment were analyzed in detail using the finite element method. The results showed that the crease formed on the lateral side near the edge of the plate as a result of uneven stress during broadside rolling. The creases rose to the surface with unrestricted spread and evolved into a straight edge seam during the subsequent straight rolling. To eliminate the straight edge seam defect, chamfered slabs were developed and investigated for rolling. The use of the chamfered slabs provided two advantages for rolling: the distribution of the temperature near the edge was ameliorated, and the deformation shape was improved by the chamfered shape. As a result, the risk of forming a straight edge seam defect was reduced by the use of a chamfered slab.
|
Received: 15 January 2016
Published: 12 June 2016
|
|
|
|
[1] |
Wan-ming Li,Zhou-hua Jiang,,*,Xi-min Zang,Xin Deng. Modeling of flow and temperature distribution in electroslag remelting withdrawal process for fabricating large-scale slab ingots[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 569-578. |
[2] |
Da-shan Sui,*,Hai-ming Zhang,Hong-yang Zhu,Zhe Zhu,Zhen-shan Cui. Effects of process parameters on fragment and refinement of millimeter-grade coarse grains for 316LN steel during hot cogging[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 529-535. |
[3] |
Nan-nan Zhang,*,Dan-yang Lin,Ya-li Li,Yue Zhang,Marie-pierre Planche,Han-lin Liao, Christian Coddet,Fu-yu Dong. In-flight particle characterization and coating formation under low pressure plasma spray condition[J]. Chinese Journal of Iron and Steel, 2017, 24(3): 306-312. |
[4] |
Si-qian Bao,,*,Yang Xu,Gang Zhao,,Xiang-bin Huang,Huan Xiao,Chuan-long Ye, Na-na Song,Qing-ming Chang. Microstructure, texture and precipitates of grain-oriented silicon steel produced by thin slab casting and rolling process[J]. Chinese Journal of Iron and Steel, 2017, 24(1): 91-96. |
[5] |
Zheng CHEN,,Qi��jie ZHAI,Jie��yu ZHANG,Hong��gang ZHONG. Effects of Thermal Gradients and Rotational Flows on Grain Growth in 22 t Steel Ingots[J]. Chinese Journal of Iron and Steel, 2016, 23(9): 973-980. |
[6] |
Nan WANG,Jin XU,Shan YU,Guang-zong ZHANG,Guang-hao CHEN,Min CHEN. Effect of Scale Formation on Copper Enrichment Behavior in Continuously Cast Slab[J]. Chinese Journal of Iron and Steel, 2016, 23(8): 739-744. |
|
|
|
|