Effect of Alloying Method on Microstructure and Wear Resistance of Fe-Cr-V-B Based Alloy |
Yu MA,Ying LIU,Jun LI,Hui ZHANG,Hao YANG |
School of Materials Science and Engineering, Sichuan University, Chengdu 610065, Sichuan, China |
|
|
Abstract The microstructure and wear behavior of Fe-Cr-V-B based alloy was investigated. Each of the specimens was characterized by metallographic techniques and hardness test. Phase analysis of alloy was performed by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). The results showed that the microstructure of Fe-Cr-V-B based as-cast alloy containing 8.6 mass% V was composed of ��-(Fe,Cr) solid solution, VC carbides, and V3B4 borides, whereas the as-cast alloy containing 24.8 mass% Cr was composed of ��-(Fe,Cr) solid solution and V3B4 borides; the eutectic V3B4 borides mainly comprise M2B-type borides (M presents Fe and Cr). The existence of a large amount of V atoms affects the growth pattern of eutectic borides, which mainly display rod-like and grainy structure. The wear behavior of the experimental alloy has been investigated using pin-on-disk type friction and wear apparatus. The comparison of experimental results indicated that the relative wear resistance of the alloy containing 8.6 mass% V after destabilization heat treatment in a conventional furnace at 1373 K for 2 h was about six times higher than that of the high chromium (19 mass%) cast iron.
|
Received: 15 May 2015
Published: 12 June 2016
|
Corresponding Authors:
Yu Ma
E-mail: 79588715@qq.com
|
|
|
|
[1] |
Ying Ci,*,Zhan-zhan Zhang. Simulation study on heat-affected zone of high-strain X80 pipeline steel[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 966-973. |
[2] |
Xiao-li Zhao,,Yong-jian Zhang,Cheng-wei Shao,Wei-jun Hui,Han Dong. Thermal stability of retained austenite and mechanical properties of medium-Mn steel during tempering treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 830-837. |
[3] |
Xu Yang,,Bo Liao,Fu-ren Xiao,Wei Yan,Yi-yin Shan,Ke Yang. Ripening behavior of M23C6 carbides in P92 steel during aging at 800��C[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 858-864. |
[4] |
Hang-wei Zhou,,Hui-qun Liu,,Dan-qing Yi,,Yu Xiao,,Xiao-long Zhao,Jian Wang,Qi Gao. Effect of �� phase on fatigue crack growth of Ti-6242 alloy[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 811-822. |
[5] |
Reng-chong Xu,,Yan-lin He,,Hu Jiang,,Hua Wang,,Na-qiong Zhu,,Xiao-gang Lu,, Lin Li,. Microstructures and mechanical properties of ferrite-based lightweight steel with different compositions[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 737-742. |
[6] |
Wei-jun Hui,*,Na Xiao,Xiao-li Zhao,Yong-jian Zhang,Yu-feng Wu. Effect of vanadium on dynamic continuous cooling transformation behavior of medium-carbon forging steels[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 641-648. |
|
|
|
|