Effects of Nb and V on Microstructural Evolution, Precipitation Behavior and Tensile Properties in Hot-rolled Mo-bearing Steel |
Fu-ming LIU1,Jian-jun WANG1,2,Yu-jie LIU1,R.D.K. MISRA3,Chun-ming LIU1,2 |
1. School of Materials Science and Engineering, Northeastern University, Shenyang 110819, Liaoning, China 2. Key Laboratory for Anisotropy and Texture of Materials of Ministry of Education, Northeastern University,Shenyang 110819, Liaoning, China 3. Laboratory for Excellence in Advanced Steel Research, Department of Metallurgical and Materials Engineering, University of Texas at El Paso, TX 79968-0521, USA |
|
|
Abstract Microstructural evolution, precipitation behavior, and tensile properties of four experimental Mo-bearing steels were studied to elucidate the effects of Nb and V on microstructural properties. The results indicated that the microstructure of hot-rolled steels consisted of polygonal ferrite and degenerate pearlite, and the morphology remained same after holding at 600 �� for 1 h. The smallest grain size was obtained in Nb-V-Mo containing steel, followed by Nb-Mo and V-Mo steels. Precipitation was less in the hot-rolled Mo-bearing steel. The maximum volume fraction of precipitates was obtained in Nb-V-Mo bearing steel, and the Nb-V-Mo complex carbonitrides were highly stable at 600 ��. In the Mo-bearing steel, the yield ratio was lowest at room temperature but highest at 600 ��, which was attributed to the precipitation of Mo carbides and drag effect of Mo solute on dislocation movement.
|
Received: 01 December 2015
Published: 12 June 2016
|
Fund:the National Key Technology Research and Development Program of the Ministry of Science and Technology of China;the Fundamental Research Funds for the Central Universities |
|
|
|
[1] |
Zhong-liang Tian,,Sen-bao Jiang,Zheng-zong Chen,Han-sheng Bao,Zheng-dong Liu,*. Microstructural evolution and mechanical properties of a new Ni-based heat-resistant alloy during aging at 750��C[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 513-519. |
[2] |
Xue-feng Peng,Jing Liu,*,Jing-tao Han,Dong-bin Wei. Effect of hot/warm roll-forming process on microstructural evolution and mechanical properties of local thickened U-rib for orthotropic steel deck[J]. Chinese Journal of Iron and Steel, 2017, 24(3): 335-342. |
[3] |
Ying KAN,,Shi-hong ZHANG,Li-wen ZHANG,Ming CHENG,Hong-wu SONG,Hong-wei LU. Healing Behavior of Micropores in Powder Metallurgy 316L Stainless Steel during Hot Forging and Heat Treatment[J]. Chinese Journal of Iron and Steel, 2014, 21(9): 862-868. |
[4] |
Rong-sheng QI,Bao-feng GUO,Xin-gang LIU,Miao JIN. Flow Stress Behaviors and Microstructure Evolution of 300M High Strength Steel under Isothermal Compression[J]. Chinese Journal of Iron and Steel, 2014, 21(12): 1116-1123. |
[5] |
YU Hai-yan. Microscopic Response of TRIP Steels to Prestrain During Plastic Deformation[J]. Chinese Journal of Iron and Steel, 2013, 20(9): 80-85. |
[6] |
LIU Qing-you SUN Xin-jun JIA Shu-jun ZHANG Lu-lin HUANG Guo-jian REN Yi. Austenitization Behaviors of X80 Pipeline Steels With High Nb and Micro-Ti Treatment[J]. Chinese Journal of Iron and Steel, 2009, 16(6): 58-62. |
|
|
|
|