Effect of 0��5 mass% Cu Addition on Ductility and Magnetic Properties of Fe-6��5Si Alloy |
Zhao-yang CHENG,Jing LIU,Wen-si CHEN,Jia-chen ZHU,Xi-feng LIN,Zhi-dong XIANG |
The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science andTechnology, Wuhan 430081, Hubei, China |
|
|
Abstract The effect of adding 0��5 mass% Cu on ductility and magnetic properties of Fe-6��5Si (mass%) alloy was investigated. The alloys with and without 0��5 mass% Cu addition were warm rolled into thin sheets of thickness no more than 0��3 mm at temperature below 600 ��. It was found that the alloy with 0��5 mass% Cu addition was more easily warm rolled than Cu-free alloy. Tensile tests were carried out to further investigate this phenomenon, which confirmed that the ductility of the alloy with 0��5 mass% Cu addition was significantly higher than that of Cu-free alloy at 550 ��. Based on the results of transmission electron microscopy analysis, the ductility increase of the alloy with 0��5 mass% Cu addition was attributed to the effect of Cu on the promotion of dynamic recovery and suppression of long-range order in the alloy during warm rolling process. It was also observed that the iron loss was lower and inductance was higher for the alloy with 0��5 mass% Cu addition. Thus, it can be concluded that adding a suitably small amount of Cu would not only increase the ductility of Fe-6��5Si alloy at warm rolling temperatures but also improve its magnetic properties.
|
Received: 23 July 2015
Published: 01 July 2016
|
Fund:the National Basic Research Program (863 Program) of China;the Provincial Natural Science Foundation of Hubei, China |
|
|
|
[1] |
Ying Ci,*,Zhan-zhan Zhang. Simulation study on heat-affected zone of high-strain X80 pipeline steel[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 966-973. |
[2] |
Xiao-li Zhao,,Yong-jian Zhang,Cheng-wei Shao,Wei-jun Hui,Han Dong. Thermal stability of retained austenite and mechanical properties of medium-Mn steel during tempering treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 830-837. |
[3] |
Hang-wei Zhou,,Hui-qun Liu,,Dan-qing Yi,,Yu Xiao,,Xiao-long Zhao,Jian Wang,Qi Gao. Effect of �� phase on fatigue crack growth of Ti-6242 alloy[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 811-822. |
[4] |
Reng-chong Xu,,Yan-lin He,,Hu Jiang,,Hua Wang,,Na-qiong Zhu,,Xiao-gang Lu,, Lin Li,. Microstructures and mechanical properties of ferrite-based lightweight steel with different compositions[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 737-742. |
[5] |
Wei-jun Hui,*,Na Xiao,Xiao-li Zhao,Yong-jian Zhang,Yu-feng Wu. Effect of vanadium on dynamic continuous cooling transformation behavior of medium-carbon forging steels[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 641-648. |
[6] |
Yong-xing Jiao,Jian-sheng Liu*,Xing-wang Duan,Xiao-hua Zheng,Wen-wu He. Prediction of critical forging penetration efficiency for 06Cr19Ni9NbN steel by dynamic recrystallization[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 649-653. |
|
|
|
|