Viscosity and Structure Changes of CaO-SiO2-Al2O3-CaF2 Melts with Substituting Al2O3 for SiO2 |
Guo-hua ZHANG,Yu-lan ZHEN,Kuo-chih CHOU |
State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China |
|
|
Abstract During the smelting process of the high Al steels, the reaction between SiO2 in molten slag and dissolved aluminum in liquid steel always takes place. This aluminathermic reduction reaction will lead to the substitution of 1 mol SiO2 for 2/3 mol Al2O3. Therefore, the investigations about the influence of the ratio of Al2O3 to SiO2 on viscosity and structure changes of mould flux during this process are very necessary. The viscosity variation of CaO-SiO2-Al2O3-CaF2 melts was studied by changing compositions considering the aluminathermic reduction reaction. It was found that viscosity increased monotonously with gradually increasing the substitution extent. According to the Raman analysis, the substitution of Al2O3 for SiO2 leads to the decrease of non-bridging oxygen but the increase of bridging oxygen. Therefore, degree of polymerization and viscosity increase as the substitution extent increases. By comparing the measured viscosities with the model calculated values, it was found that both the recently developed Zhang��s model and Roboud model could describe the viscosity variation behavior of CaO-SiO2-Al2O3-CaF2 melts very well.
|
Received: 12 June 2015
Published: 01 July 2016
|
|
|
|
[1] |
Sheng-feng Guo,*,Chen Su,Jia-xiang Cui,Jing Li,Guan-nan Li,Meng Zhang,Ning Li. Effects of B addition on glass forming ability and thermal behavior of FePC-based bulk metallic glasses[J]. Chinese Journal of Iron and Steel, 2017, 24(4): 442-447. |
[2] |
Hui GAO,Bang-shao DONG,Shao-xiong ZHOU. Advances in Investigation of Fe-based Glass-forming Alloy Melts[J]. Chinese Journal of Iron and Steel, 2016, 23(6): 509-515. |
[3] |
Chen-xi JI , Yang CUI, Zhi ZENG, Zhi-hong TIAN, Chang-liang ZHAO , Guo-sen ZHU. Continuous Casting of High-Al Steel in Shougang Jingtang Steel Works[J]. Chinese Journal of Iron and Steel, 2015, 22(Supplement 1): 53-56. |
[4] |
Ji��fang XU,Li��juan SU,Dong CHEN,Jie��yu ZHANG,Yao CHEN. Experimental Investigation on Viscosity of CaO��MgO(��Al2O3)��SiO2 Slags and Solid��liquid Mixtures[J]. Chinese Journal of Iron and Steel, 2015, 22(12): 1091-1097. |
[5] |
QIU Xin,XIE Bing,QING Xue-mei,DIAO Jiang,HUANG Qing-yun,WANG Shui-bo. Effects of Transition Metal Oxides on Thermal Conductivity of Mould Fluxes[J]. Chinese Journal of Iron and Steel, 2013, 20(11): 27-32. |
[6] |
WANG Qian,LU Yong��jian,HE Sheng��ping,WANG Li��juan,K C Mills. Development of Test Method for Measuring Sintering Temperature of Mould Fluxes[J]. Chinese Journal of Iron and Steel, 2011, 18(4): 1-6. |
|
|
|
|