| Influences of Technological Parameters on Smelting-separation Process for Metallized Pellets of Vanadium-bearing Titanomagnetite Concentrates |
| En-hui WU1,2,Rong ZHU1,Shao-li YANG2,Lan MA2,Jun LI2,Jing HOU2 |
1. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083,China
2. Innovation and Technology Center of Panxi, Panzhihua University, Panzhihua 617000, Sichuan, China |
|
|
|
|
Abstract The smelting-separation process for metallized pellets of vanadium-bearing titanomagnetite concentrates was studied. The influences of smelting temperature, smelting time, and the basicity of the metallized pellet on vanadium and iron recovery were investigated. The characteristics of titanium slag were analyzed using X-ray diffraction, energy dispersive spectroscopy, and mineralographic microscopic analysis. The results demonstrate that appropriate increases in smelting temperature and smelting time can improve the vanadium and iron recovery from metallized pellets and are beneficial for the slag-iron separation. Although increasing the basicity of the metallized pellet can considerably improve the vanadium and iron recovery, the TiO2 grade of titanium slag was decreased. Under the optimal conditions, 90��17% of vanadium and 92��98% of iron in the metallized pellet were recovered, and the TiO2 grade of titanium slag was 55��01%. It was found that anosovite, augite, spinel, glassiness, and metallic iron were the main mineral phases of the titanium slag.
|
|
Received: 11 August 2015
Published: 01 July 2016
|
| Fund:��������������̼���Ŵ���-��ԭ-������Ļ����о� |
|
|
|
| [1] |
Wei-jun Hui,*,Na Xiao,Xiao-li Zhao,Yong-jian Zhang,Yu-feng Wu. Effect of vanadium on dynamic continuous cooling transformation behavior of medium-carbon forging steels[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 641-648. |
| [2] |
Cheng-song Liu,Xiao-qin Liu,*,Hong-wei Ni,Shu-feng Yang,Jing-she Li,Fei Ye. Effect of vanadium on modification of inclusions in Mn- and Si-deoxidized steel during heat treatment at 1473 K[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 520-528. |
| [3] |
Wei Li,Gui-qin Fu,Man-sheng Chu,Miao-yong Zhu*. Reduction behavior and mechanism of Hongge vanadium titanomagnetite pellets by gas mixture of H2 and CO[J]. Chinese Journal of Iron and Steel, 2017, 24(1): 34-42. |
| [4] |
Wei-jun HUI,Cheng-wei SHAO,Yong-jian ZHANG,Si-lian CHEN,Han DONG. Influence of Vanadium on Fracture Splitting Property of Medium Carbon Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(5): 475-483. |
| [5] |
Shuang-yin CHEN,Xiao-jiao FU,Man-sheng CHU,Xi-zhe LI,Zheng-gen LIU,Jue TANG. Carbothermic Reduction Mechanism of Vanadium-titanium Magnetite[J]. Chinese Journal of Iron and Steel, 2016, 23(5): 409-414. |
| [6] |
Feng PAN,Qing-shan ZHU,Zhan DU,,Hao-yan SUN. Oxidation Kinetics, Structural Changes and Element Migration during Oxidation Process of Vanadium-titanium Magnetite Ore[J]. Chinese Journal of Iron and Steel, 2016, 23(11): 1160-1167. |
|
|
|
|
2016, Vol. 23 