| Constitutive Model of Warm Deformation Behavior of Medium Carbon Steel |
| Hong��bin LI1,2,Yun��li FENG2,Tao YAN3,En��lin YU1 |
1. National Engineering Research Center for Equipment and Technology of Cold Strip Rolling, Yanshan University,Qinhuangdao 066004, Hebei, China
2. College of Metallurgy and Energy, North China University of Science and Technology, Tangshan 063009, Hebei, China
3. Equipment Manufacturing College, Hebei University of Engineering, Handan 056038, Hebei, China |
|
|
|
|
Abstract The compressive behaviors of medium carbon steel specimens were investigated over a wide range of temperatures and strain rates using a Gleeble��3500 thermo��simulation machine. The results show that the flow stress increased with strain at first, and then gradually decreased after reaching a peak value. The flow stress softening rate at a high strain rate was larger than that at a low strain rate. The effects of deformation heating and friction on flow stress were analyzed. A new friction correction method, wherein the effect of strain on frictional coefficient was considered, was established here. The stresses revised by the new method deviated from the measured stresses with increasing strain. Meanwhile, the apparent frictional coefficient variation law with strain was obtained. The frictional coefficient increased as the strain increased and then slightly decreased after maintaining a constant value. The stress was corrected by considering deformation heating. The accuracy of the temperature correction method was verified using a special experiment. The results of the verification experiment show that the temperature correction method exhibited a good accuracy in calculating the variation of stress caused by deformation heating. A constitutive model considering strain was proposed here to describe the deformation behaviors. Compared with experimental data, the modified constitutive model exhibited a good accuracy as to constitutive correlation.
|
|
Received: 30 December 2015
Published: 02 September 2016
|
|
Corresponding Authors:
Hongbin Li
E-mail: lihongbinxp@126.com
|
|
|
|
| [1] |
Yang Yun,Qing-wu Cai,,Bao-sheng Xie,*,Shuang Li. Effect of tempering temperature on strain hardening exponent and flow stress curve of 1000 MPa grade steel for construction machinery[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 950-956. |
| [2] |
Yuan-ji Shi,Lan-ji Liu,Lei Zhang,Li-jun Zhang,Li Zheng,Run-xia Li,Bao-yi Yu*. Effect of squeeze casting process on microstructures and flow stress behavior of Al-17.5Si-4Cu-0.5Mg alloy[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 957-965. |
| [3] |
Lei Wang,Di Tang*,Yong Song. Prediction of mechanical behavior of ferrite-pearlite steel[J]. Chinese Journal of Iron and Steel, 2017, 24(3): 321-327. |
| [4] |
Bao- sheng XIE,Qing- wu CAI,Wei YU,Shi- xin XU,Ban WANG. A Flow Stress Model for High Strength Steels with Low Carbon Bainite Structure[J]. Chinese Journal of Iron and Steel, 2016, 23(4): 372-379. |
| [5] |
Fei GAO,Fu-xiao YU,Hai-tao LIU,Zhen-yu LIU. Hot Deformation Behavior and Flow Stress Prediction of Ultra Purified 17% Cr Ferritic Stainless Steel Stabilized with Nb and Ti[J]. Chinese Journal of Iron and Steel, 2015, 22(9): 827-836. |
| [6] |
Fei CHEN,,Fa-cai REN,Zhen-shan CUI,Xin-min LAI. Constitutive Modeling for Elevated Temperature Flow Behavior of 30Cr2Ni4MoV Ultra-super-critical Rotor Steel[J]. Chinese Journal of Iron and Steel, 2014, 21(5): 521-526. |
|
|
|
|
2016, Vol. 23 