| Unexpected Effect of Nb Addition as a Microalloying Element on Mechanical Properties of �Ī�TRIP Steels |
| Sajad Gholami SHIRI1,Seyed Ahmad Jenabali JAHROMI1,Yahya PALIZDAR2,Majid BELBASI3 |
1. Department of Materials Science & Engineering, School of Engineering, Shiraz University, Shiraz 115019, Iran
2. Nanotechnology and Advanced Materials Department, Materials and Energy Research Center, Karaj 128747, Iran
3. Department of Materials Engineering, Islamic Azad University Central Tehran Branch, Tehran 009821, Iran |
|
|
|
|
Abstract The concept of microalloying was applied to the �Ī�TRIP (transformation��induced plasticity) steel to investigate the feasibility of increasing the mechanical properties and understanding the effect of microalloying on the morphology and structure of the steel. A hot rolled �Ī�TRIP steel with three different contents of Nb (0, 0��03, 0��07 mass%) was subjected to the microstructural and mechanical examination. The high Al and Si concentration in these steels guaranteed the presence of the considerable �Ī�ferrite phase in the microstructure after the casting and the subsequent hot rolling. The obtained results showed that Nb dramatically affects the microstructure, the dynamic recovery and recrystallization behavior, as well as the grain shape and thus the stability of austenite after the thermomechanical process of hot rolling. The results also revealed an unexpected effect of Nb on the mechanical properties. The addition of Nb to the �Ī�TRIP steel led to a significant decrease in the ultimate strength (from 1144 to 917 MPa) and an increase in ductility (from 24% to 28%). These unconventional results could be explained by the change in the steel microstructure. The work��hardening behaviors of all samples exhibit three stages of the work��hardening rate evolution. At the stage 2, the work��hardening rate of the studied steels increased, being attributed to the TRIP effect and the transformation of austenite to martensite.
|
|
Received: 16 February 2016
Published: 02 September 2016
|
| Fund:Shiraz Univercity Ph.D. Funds |
|
|
|
|
|
|
2016, Vol. 23 