| Effect of Al2O3 modification on enrichment and stabilization of chromium in stainless steel slag |
| Long-hu Cao,Cheng-jun Liu*,Qing Zhao,Mao-fa Jiang |
| Key Laboratory for Ecological Metallurgy of Multimetallic Mineral Ministry of Education, Northeastern University, Shenyang 110819, Liaoning, China |
|
|
|
|
Abstract Spinel phase is considered to be the optimal phase for stabilization of chromium in stainless steel slag. In order to restrain chromium leaching from slag for the effective environmental protection, Al2O3 was utilized for the modification treatment, and the effects on the enrichment and stabilization of chromium were investigated. The mineral phases and the existence state of chromium in slag with various Al2O3 contents at different basicities (wCaO/wSiO2) were analyzed by scanning electron microscopy-energy dispersive spectroscopy (SEM-EDS) and X-ray diffraction (XRD). The results showed that chromium mainly existed in the glass and spinel phases at basicity of 1.0 and 1.5. As the slag basicity increased to 2.0, chromium was also found in periclase phase. Al2O3 in the stainless steel slag reacted with MgO and Cr2O3, which could generate the Al-rich Mg(CrxAl1-x)2O4 solid solution. Moreover, the addition of Al2O3 was favorable to reduce the solubility of chromium oxide in liquid phase and suppress the precipitation of periclase phase. The experimental results demonstrated that Al2O3 modification has a positive influence on the enrichment and the stabilization of chromium in the stainless steel slag.
|
|
Received: 28 June 2016
Published: 20 March 2017
|
| Fund:National Nature Science Foundation of China;National Natural Science Foundation of China |
|
Corresponding Authors:
Liu
E-mail: 670372720@qq.com
|
|
|
|
| [1] |
Qiang Zheng,Xue Bian,Wen-yuan Wu*. Iron recovery and rare earths enrichment from Bayan Obo tailings using Coal-Ca(OH)2-NaOH roasting followed by magnetic separation[J]. Chinese Journal of Iron and Steel, 2017, 24(2): 147-155. |
| [2] |
Hai-feng Xu,,*,Feng Yu,Chang Wang,Wan-li Zhang,Jian Li,Wen-quan Cao. Comparison of microstructure and property of high chromium bearing steel with and without nitrogen addition[J]. Chinese Journal of Iron and Steel, 2017, 24(2): 206-213. |
| [3] |
Dong��ping ZHAN,Yang��peng ZHANG,Zhou��hua JIANG,De��wei WANG,Hui��shu ZHANG. Chromium Recycling from Argon��oxygen Decarburization Dust in Hot Metal Pre��dephosphorization Process[J]. Chinese Journal of Iron and Steel, 2016, 23(9): 867-873. |
| [4] |
Bao-chao ZHENG,Zhi-fu HUANG,Jian-dong XING,Yi-yang XIAO,Xiao FAN,Yong WANG. Effects of Chromium Addition on Preparation and Properties of Bulk Cementite[J]. Chinese Journal of Iron and Steel, 2016, 23(8): 842-850. |
| [5] |
Nan WANG,Jin XU,Shan YU,Guang-zong ZHANG,Guang-hao CHEN,Min CHEN. Effect of Scale Formation on Copper Enrichment Behavior in Continuously Cast Slab[J]. Chinese Journal of Iron and Steel, 2016, 23(8): 739-744. |
| [6] |
Yang-bo LIU,,Wei ZHANG,Qian TONG,Qi-song SUN. Effects of Si and Cr on Complete Decarburization Behavior of High Carbon Steels in Atmosphere of 2 vol.% O2[J]. Chinese Journal of Iron and Steel, 2016, 23(12): 1316-1322. |
|
|
|
|
2017, Vol. 24 