Prediction of mechanical behavior of ferrite-pearlite steel |
Lei Wang,Di Tang*,Yong Song |
Institute of Engineering Technology, University of Science and Technology Beijing, Beijing 100083, China |
|
|
Abstract A new approach describing the flow stress of ferrite-pearlite steel has been proposed, which divided the deformation process into three stages based on whether ferrite or pearlite yielded. Iso-work increment assumption was applied to describe the transfer of load between the components. The physically based model to describe ferrite was approximated with Swift��s equation in order to obtain the analytic solution. The tensile strength of ferrite-pearlite had a linear relation with pearlite volume fraction, square root reciprocal of ferrite grain size and reciprocal of pearlite interlamellar spacing. Moreover, a model to calculate the tensile strength of ferrite-pearlite steel was proposed. The predicted values of tensile strength were in good agreement with experimental results when the pearlite volume fraction was less than 20%. Considering the plastic relaxation mechanisms, the internal stress was modified with pearlite volume fraction, total strain, yield stress of ferrite and pearlite when the pearlite volume fraction was more than 20%.
|
Received: 25 August 2016
Published: 20 March 2017
|
Fund:the Fundamental Research Funds for the Central Universities |
Corresponding Authors:
Lei Wang
E-mail: emily277@163.com
|
|
|
|
[1] |
Yang Yun,Qing-wu Cai,,Bao-sheng Xie,*,Shuang Li. Effect of tempering temperature on strain hardening exponent and flow stress curve of 1000 MPa grade steel for construction machinery[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 950-956. |
[2] |
Yuan-ji Shi,Lan-ji Liu,Lei Zhang,Li-jun Zhang,Li Zheng,Run-xia Li,Bao-yi Yu*. Effect of squeeze casting process on microstructures and flow stress behavior of Al-17.5Si-4Cu-0.5Mg alloy[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 957-965. |
[3] |
Qi-long Yong,,*,Zheng-yan Zhang,Xin-jun Sun,Jian-chun Cao,Zhao-dong Li. Effect of dissolved niobium on eutectoid transformation behavior[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 973-980. |
[4] |
Li-jun Xu,Shu-lan Zhang,Chun-gen Qiu,Sheng-tao Qiu,Xing-zhong Zhang. Surface microstructure control of microalloyed steel during slab casting[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 803-810. |
[5] |
Reng-chong Xu,,Yan-lin He,,Hu Jiang,,Hua Wang,,Na-qiong Zhu,,Xiao-gang Lu,, Lin Li,. Microstructures and mechanical properties of ferrite-based lightweight steel with different compositions[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 737-742. |
[6] |
Rui-bin Gou,,,Wen-jiao Dan,,Wei-gang Zhang,,Min Yu,*,Chun-yu Zhang,Yin-hu Qiao, Lu Ma. Microstructure failure in ferrite-martensite dual phase steel under in-situ tensile test[J]. Chinese Journal of Iron and Steel, 2017, 24(3): 350-356. |
|
|
|
|