Tailored properties of a novelly-designed press-hardened 22MnMoB steel |
Ming-bo Zhou1,Jing-lin Tang1,*,Jie Yang2,Cun-yu Wang3 |
1 Key Laboratory of Advanced Forging & Stamping Technology and Science Yanshan University, Ministry of Education of China, Qinhuangdao 066004, Hebei, China 2 Lightweight Research Department, Society of Automotive Engineers of China, Beijing 100055, China 3 Central Iron & Steel Research Institute, Beijing 100081, China |
|
|
Abstract A novel 22MnMoB hot stamping steel was designed. The continuous cooling transformation (CCT) measurement of the 22MnMoB steel showed that the ferrite-bainite microstructure could be obtained at cooling rates lower than 25��C/s, and the complete martensite structure required the cooling rate higher than 30��C/s. The experiments with non-uniform die temperatures were carried out to obtain tailored properties. The results showed that strength of 1411 MPa and elongation of 6% could be obtained in the hard zone, and strength of 916 MPa and elongation of 9% could be obtained in the soft zone, which can be realized by controlling the die temperature at 400��C. The transition zone was found smooth and could be beneficial to reduce the stress concentration and therefore improve the performance of components.
|
Received: 04 January 2017
Published: 12 May 2017
|
Fund:National Natural Science Foundation of China;Fundamental Research Funds for the Central Universities |
Corresponding Authors:
������ MingBo
E-mail: mbzhou@163.com
|
|
|
|
[1] |
Ying Ci,*,Zhan-zhan Zhang. Simulation study on heat-affected zone of high-strain X80 pipeline steel[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 966-973. |
[2] |
Xiao-li Zhao,,Yong-jian Zhang,Cheng-wei Shao,Wei-jun Hui,Han Dong. Thermal stability of retained austenite and mechanical properties of medium-Mn steel during tempering treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 830-837. |
[3] |
Hong-ru Ren,Jin-tao Gao,Zhe Wang,Chong Li,Fu-qiang Wang,Zhan-cheng Guo. Evolution of microstructure, mechanical and magnetic properties of electrodeposited 50%Ni-Fe alloy foil after thermal treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 844-851. |
[4] |
Hang-wei Zhou,,Hui-qun Liu,,Dan-qing Yi,,Yu Xiao,,Xiao-long Zhao,Jian Wang,Qi Gao. Effect of �� phase on fatigue crack growth of Ti-6242 alloy[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 811-822. |
[5] |
Reng-chong Xu,,Yan-lin He,,Hu Jiang,,Hua Wang,,Na-qiong Zhu,,Xiao-gang Lu,, Lin Li,. Microstructures and mechanical properties of ferrite-based lightweight steel with different compositions[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 737-742. |
[6] |
Wei-jun Hui,*,Na Xiao,Xiao-li Zhao,Yong-jian Zhang,Yu-feng Wu. Effect of vanadium on dynamic continuous cooling transformation behavior of medium-carbon forging steels[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 641-648. |
|
|
|
|