| Effect of vanadium on modification of inclusions in Mn- and Si-deoxidized steel during heat treatment at 1473 K |
| Cheng-song Liu1,Xiao-qin Liu1,*,Hong-wei Ni1,Shu-feng Yang2,Jing-she Li2,Fei Ye1 |
1 The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081,Hubei, China
2 School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China |
|
|
|
|
Abstract The effect of vanadium (V) on the modification of oxide inclusions in steels with different concentrations of Mn, Si, and V was determined before and after heat treatment at 1473 K. Changes in the morphology, size, and composition of these inclusions were analyzed. Equilibrium relations between the inclusions and steels at 1873 K and 1473 K were calculated using available thermodynamic data to roughly approximate the stable oxide inclusions in the steels. The results revealed that the concentrations of V and Si in the steel are critical for controlling the modification of the inclusions during heat treatment at 1473 K. MnO-SiO2-type oxide inclusions gradually transformed into MnO-V2O3-type or Mn-SiO2- and MnO-V2O3-type inclusions in low-Si high-V steels heat-treated for 60 min. In addition, the morphology of the inclusions changed from spherical to irregular. A Si-accumulated zone and a V-depleted zone formed close to the interface in the steel matrix. The experimental and calculation results indicated that, during the heat treatment, an interface chemical reaction occurred between the Fe-Mn-Si-V steel and the MnO-SiO2-type oxide inclusion.
|
|
Received: 22 August 2016
Published: 12 May 2017
|
| Fund:Chinese National Natural Science Foundation;Chinese National Natural Science Foundation |
|
Corresponding Authors:
Cheng-Song LIU
E-mail: chengsongliu@126.com
|
|
|
|
| [1] |
Min-qiang Gao,Ying-dong Qu,Guang-long Li,Jun-hua You,Rong-de Li. Cementites decomposition of a pearlitic ductile cast iron during graphitization annealing heat treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 838-843. |
| [2] |
Zhu-jun Jiang,Yu-ye Wu,,Jing-min Wang,Cheng-bao Jiang. Influence of cooling rate on magneto-structural transition and magnetocaloric effect of Ni30Cu8Co12Mn37Ga13 alloy[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 711-717. |
| [3] |
Wei-jun Hui,*,Na Xiao,Xiao-li Zhao,Yong-jian Zhang,Yu-feng Wu. Effect of vanadium on dynamic continuous cooling transformation behavior of medium-carbon forging steels[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 641-648. |
| [4] |
Pei-sheng Liu*,Guang Cui,Yi-jiao Guo,Jing-he Chen,Zi-xuan Yang. A novel sort of porous ceramic foam ball with modified surface for arsenic removal from aqueous solution[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 661-667. |
| [5] |
Yong-jiang Huang,,,*,Peng Xue,Xiang Cheng,Ya-ming Wang,Fu-yang Cao,**, Zhi-liang Ning, Jian-fei Sun,. Plasticity improvement of a Zr-based bulk metallic glass by micro-arc oxidation[J]. Chinese Journal of Iron and Steel, 2017, 24(4): 416-420. |
| [6] |
Long-hu Cao,Cheng-jun Liu*,Qing Zhao,Mao-fa Jiang. Effect of Al2O3 modification on enrichment and stabilization of chromium in stainless steel slag[J]. Chinese Journal of Iron and Steel, 2017, 24(3): 258-265. |
|
|
|
|
2017, Vol. 24 