| Effects of process parameters on fragment and refinement of millimeter-grade coarse grains for 316LN steel during hot cogging |
| Da-shan Sui1,*,Hai-ming Zhang1,Hong-yang Zhu2,Zhe Zhu1,Zhen-shan Cui1 |
1 National Die & Mold CAD Engineering Research Center, Shanghai Jiao Tong University, Shanghai 200030, China
2 Shanghai Heavy Machinery Plant, Shanghai 200245, China |
|
|
|
|
Abstract The heterogeneous mixed-grain microstructure is a common defect for the heavy forging of 316LN austenitic stainless steel. Isothermal compression experiments were performed on a Gleeble-3500 thermo-mechanical simulator to investigate the effect of process parameters on the fragment and refinement of millimeter-grade coarse grains (MCGs) during hot cogging. The experimental results indicate that the stress of MCG specimens is much larger than that of fine grain (FG) ones at 1150��C, while the stress difference between MCG and FG samples became smaller at 1200��C. Moreover, the MCGs can be well fragmented and refined under the condition of temperature of 1200��C, strain rate of 0��01 s-1, and reduction rate of 50%. Meanwhile, numerical simulations were conducted to study the influences of temperature, strain and strain rate on microstructure evolution. The results of experiments and simulations comprehensively demonstrate that the MCG results in the increase of deformation resistance and incompatibility of deformation, and it can be fragmented and refined at 1200��C so that the plastic deformation energy decreases remarkably with the increase of temperature from 1150 to 1200��C.
|
|
Received: 25 August 2016
Published: 12 May 2017
|
| Fund:National Basic Research Program of China |
|
Corresponding Authors:
Da-shan SUI
E-mail: dasui@sjtu.edu.cn
|
|
|
|
| [1] |
Zhao-xia Shi,,*,Xiao-feng Yan,Chun-hua Duan,Jin-gui Song,Ming-han Zhao,Jue Wang. Hot deformation behavior of GH4945 superalloy using constitutive equation and processing map[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 625-633. |
| [2] |
Yong-xing Jiao,Jian-sheng Liu*,Xing-wang Duan,Xiao-hua Zheng,Wen-wu He. Prediction of critical forging penetration efficiency for 06Cr19Ni9NbN steel by dynamic recrystallization[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 649-653. |
| [3] |
Peng Zhou,,Qing-xian Ma,,*. Static recrystallization behavior of 25CrMo4 mirror plate steel during two-pass hot deformation[J]. Chinese Journal of Iron and Steel, 2017, 24(2): 222-228. |
| [4] |
Zheng-wei GU,,Meng-meng L��,,Xin LI,,Hong XU,. Stretch Bending of Z-section Stainless Steel Profile[J]. Chinese Journal of Iron and Steel, 2016, 23(6): 525-530. |
| [5] |
Lin LU,Long-gang HOU,Hua CUI,Jin-feng HUANG,Yong-an ZHANG,Ji-shan ZHANG. Hot Deformation Behavior and Processing Map of Spray Formed M3��2 High Speed Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(5): 501-508. |
| [6] |
Cun-jiang TANG,Shi-long LIU,Cheng-jia SHANG. Micromechanical Behavior and Failure Mechanism of F/B Multi-phase High Performance Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(5): 489-494. |
|
|
|
|
2017, Vol. 24 