| Effects of micro-alloying and production process on precipitation behaviors and mechanical properties of HRB600 |
| Hong-bo Pan1,2,*,Meng-jiao Zhang3,Wei-ming Liu1,2,Jun Yan1,2,Hui-ting Wang3,Chang-sheng Xie3,Zhan Guo4 |
1 Key Laboratory of Metallurgical Emission Reduction & Resources Recycling of Ministry of Education, Anhui University of Technology, Ma��anshan 243002, Anhui, China
2 Anhui Province Key Laboratory of Metallurgy Engineering & Resources Recycling, Anhui University of Technology,Ma��anshan 243002, Anhui, China
3 School of Metallurgical Engineering, Anhui University of Technology, Ma��anshan 243002, Anhui, China
4 Technology Center, Ma��anshan Iron & Steel Company Limited, Ma��anshan 243000, Anhui, China |
|
|
|
|
Abstract Effects of micro-alloying elements and production process on microstructure, mechanical properties and precipitates of 600 MPa grade rebars were studied by using pilot test, metallographic observation, tensile test, thermodynamic calculation and transmission electron microscopy. The results show that the tested steels are composed of ferrite and pearlite, in which the content range of pearlite is 33%-45%. For vanadium micro-alloyed steel, interphase precipitation strengthening effect of V can be promoted and the yield strength of tested steels can be increased with increasing V content and decreasing finishing rolling temperature. The temperature of terminated cooling should be more than 700��C when the water cooling is used. When niobium is added to the steel, more coarse (Nb,V)C,N precipitates are generated at high temperature, so that the solid solubility of precipitated phases of vanadium is reduced and the precipitation strengthening effect of vanadium is weakened.
|
|
Received: 08 August 2016
Published: 12 May 2017
|
| Fund:the natural science research project of Anhui province;the science and technology research program of Anhui province |
|
|
|
| [1] |
Jin-liang Gao,*,Yan Qi,Ya-qin Li,Hong-wei Shang,Dong-liang Zhao,Yang-huan Zhang. Hydrogen storage thermodynamic and kinetic characteristics of PrMg12-type alloys synthesized by mechanical milling[J]. Chinese Journal of Iron and Steel, 2017, 24(2): 198-205. |
| [2] |
Dan SONG,,,Wei SUN,Jin-yang JIANG,Han MA,Jian-chun ZHANG,Zhao-jun CHENG. Corrosion Behavior of Cr Micro-alloyed Corrosion-resistant Rebar in Neutral Cl--containing Environment[J]. Chinese Journal of Iron and Steel, 2016, 23(6): 608-617. |
| [3] |
Ming MA,Hua DING,Zheng-you TANG,Jing-wei ZHAO,Zhou-hua JIANG,Guang-wei FAN. Effects of Temperature and Strain Rate on Flow Behavior and Microstructural Evolution of Super Duplex Stainless Steel under Hot Deformation[J]. Chinese Journal of Iron and Steel, 2016, 23(3): 244-252. |
| [4] |
Yin-tao GUO, Qian WANG, Gu-jun CHEN, Sheng-ping HE. Castability of Aluminum- and Sulfur-bearing Free-cutting Steel[J]. Chinese Journal of Iron and Steel, 2015, 22(Supplement 1): 87-92. |
| [5] |
Jae-gil JUNG,Seok-jae LEE. Prediction of Nitrogen Diffusivity in ��-ferrite Based on Thermodynamics[J]. Chinese Journal of Iron and Steel, 2015, 22(8): 743-745. |
| [6] |
Guo-cheng WANG,,,Sheng-li LI,,Xin-gang AI,,Chong-min ZHANG,,Chao-bin LAI. Characterization and Thermodynamics of Al2O3-MnO-SiO2(-MnS) Inclusion Formation in Carbon Steel Billet[J]. Chinese Journal of Iron and Steel, 2015, 22(7): 566-572. |
|
|
|
|
2017, Vol. 24 