| Prediction of critical forging penetration efficiency for 06Cr19Ni9NbN steel by dynamic recrystallization |
| Yong-xing Jiao,Jian-sheng Liu*,Xing-wang Duan,Xiao-hua Zheng,Wen-wu He |
| College of Materials Science and Engineering, Taiyuan University of Science and Technology, Taiyuan 030024, Shanxi, China |
|
|
|
|
Abstract In order to determine the critical forging penetration efficiency (FPE) of 06Cr19Ni9NbN steel, a new model was presented to describe critical FPE, which is significant to optimize the steel forging process. The plane strain compression tests were conducted to obtain the model and confirm its validity. The results indicated that the dynamic recrystallization (DRX) volume fraction increases and the grain size decreases with the rise of reduction ratio. Meanwhile, the compression process was simulated by DEFORM software. The tensile tests were conducted and the results demonstrated that the mechanical properties gradually become stable when the reduction ratio increases to 30%, 34% and 40% at 1200, 1100 and 1000��C, respectively. The calculated results based on this new model are consistent with experimental results, indicating that the model is suitable to predict the critical FPE for the steel.
|
|
Received: 08 October 2016
Published: 06 June 2017
|
| Fund:Natural Science Foundation of China |
|
Corresponding Authors:
Jiao Yongxing
E-mail: jiaoyxtust@163.com
|
|
|
|
| [1] |
Zong-ye Ding,Di Zhang,Qiao-dan Hu,,*,Long Zeng,Jian-guo Li,. Constitutive analysis and optimization on hot working parameters of as-cast high Cr ultra-super-critical rotor steel with columnar grains[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 916-924. |
| [2] |
Xiao-li Zhao,,Yong-jian Zhang,Cheng-wei Shao,Wei-jun Hui,Han Dong. Thermal stability of retained austenite and mechanical properties of medium-Mn steel during tempering treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 830-837. |
| [3] |
Hong-ru Ren,Jin-tao Gao,Zhe Wang,Chong Li,Fu-qiang Wang,Zhan-cheng Guo. Evolution of microstructure, mechanical and magnetic properties of electrodeposited 50%Ni-Fe alloy foil after thermal treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 844-851. |
| [4] |
Reng-chong Xu,,Yan-lin He,,Hu Jiang,,Hua Wang,,Na-qiong Zhu,,Xiao-gang Lu,, Lin Li,. Microstructures and mechanical properties of ferrite-based lightweight steel with different compositions[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 737-742. |
| [5] |
Ming-bo Zhou,Jing-lin Tang,*,Jie Yang,Cun-yu Wang. Tailored properties of a novelly-designed press-hardened 22MnMoB steel[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 508-512. |
| [6] |
Zhong-liang Tian,,Sen-bao Jiang,Zheng-zong Chen,Han-sheng Bao,Zheng-dong Liu,*. Microstructural evolution and mechanical properties of a new Ni-based heat-resistant alloy during aging at 750��C[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 513-519. |
|
|
|
|
2017, Vol. 24 