Precipitation behavior of titanium nitride on a primary inclusion particle during solidification of bearing steel |
Liang Yang1,2,Bryan A. Webler2,Guo-guang Cheng1 |
1 State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China 2 Center for Iron and Steelmaking Research, Department of Materials Science and Engineering, Carnegie Mellon University, Pittsburgh 15213, PA, USA |
|
|
Abstract Titanium nitride precipitation on a primary inclusion particle during solidification of bearing steel has been tracked by varying temperature in a confocal scanning violet laser microscope. Upon precipitation, an obvious growth of titanium nitride on a primary inclusion particle was observed due to the rapid solute diffusion in liquid steel. The onset of titanium nitride precipitation did not change with primary inclusion particle size, but the time of growth was greater for a smaller primary inclusion particle. Meanwhile, the particle size displayed little influence on the total precipitated amount of titanium nitride on it under the same conditions. At the later period of solidification, almost no change occurred in inclusion size, but the inclusion shape varied from circle to almost square in two-dimension, or cubic in three-dimension, to attain the equilibrium with steel.
|
Received: 08 December 2016
Published: 07 July 2017
|
|
|
|
[1] |
Yu Xu,,En-gang Wang,,*,Zhuang Li,,An-yuan Deng,. Effects of vertical electromagnetic stirring on grain refinement and macrosegregation control of bearing steel billet in continuous casting[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 483-489. |
[2] |
Hai-feng Xu,,*,Feng Yu,Chang Wang,Wan-li Zhang,Jian Li,Wen-quan Cao. Comparison of microstructure and property of high chromium bearing steel with and without nitrogen addition[J]. Chinese Journal of Iron and Steel, 2017, 24(2): 206-213. |
[3] |
Fu-ming LIU,Jian-jun WANG,,Yu-jie LIU,R.D.K. MISRA,Chun-ming LIU,. Effects of Nb and V on Microstructural Evolution, Precipitation Behavior and Tensile Properties in Hot-rolled Mo-bearing Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(6): 559-565. |
[4] |
Lu LIN,,Yan-ping BAO,Min WANG,Wei JIANG,Han-mei ZHOU. Separation and Recovery of Phosphorus from P-bearing Steelmaking Slag[J]. Chinese Journal of Iron and Steel, 2014, 21(5): 496-502. |
[5] |
Zhen-guo YANG,,Bao WANG,,Xiao-feng ZHANG,Ya-tao WANG,Hong-biao DONG,Qing LIU. Effect of Electromagnetic Stirring on Molten Steel Flow and Solidification in Bloom Mold[J]. Chinese Journal of Iron and Steel, 2014, 21(12): 1095-1103. |
[6] |
LI Dan;MIN Yong-an;WU Xiao-chun. Calculation of Austenite Formation Kinetics of Copper-Bearing Steel During Continuous Heating[J]. Chinese Journal of Iron and Steel, 2010, 17(11): 62-66. |
|
|
|
|