| Effect of artificial tribological layer on sliding wear behavior of H13 steel |
| Zhen Cao,Shu-qi Wang*,Ke-zhi Huang,Bo Zhang,Guo-hong Wen,Qiu-yang Zhang,Lan Wang |
| School of Material Science and Engineering, Jiangsu University, Zhenjiang 212013, Jiangsu, China |
|
|
|
|
Abstract An artificial tribological layer was formed on the worn surface during sliding��through supplying MoS2, Fe2O3 or their equiponderant mixtures onto the sliding interface of H13/GCr15 steels. The effect of this tribological layer on the wear behavior of H13 steel was studied. The worn surfaces and subsurfaces of H13 steel were thoroughly characterized by using X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectrometry (EDS); the wear mechanisms were explored. The research results demonstrated that tribological layer did not exist during sliding of H13 steel with no additive, but it formed with the addition of MoS2, Fe2O3 or their equiponderant mixtures. When there was no tribological layer, the wear rate rapidly increased with an increase of the load. In this case, adhesive and abrasive wear prevailed. As the additives were supplied, the artificial tribological layer was observed to be immediately formed and stably existed on worn surfaces. This tribological layer presented an obvious protective function from wear and friction. Hence, the wear rate and friction coefficient were significantly decreased. MoS2 as tribological layer seemed to present more obvious protective function than Fe2O3. By supplying their mixture, the artificial tribological layer possessed not only the load-carrying capacity of Fe2O3, but also the lubricative capacity of MoS2. These two simultaneous capacities could improve the friction and wear properties of H13 steel further.
|
|
Received: 31 October 2016
Published: 27 September 2017
|
| Fund:������Ȼ��ѧ���� |
|
|
|
| [1] |
Tian-sheng LI,,Fu-ming WANG,Chang-rong LI,Guo-qing ZHANG,Qing-yong MENG. Carbide Evolution in High Molybdenum Nb-microalloyed H13 Steel during Annealing Process[J]. Chinese Journal of Iron and Steel, 2015, 22(4): 330-336. |
| [2] |
Ting SUN,Ren-bo SONG,Xu WANG,Peng DENG,Chun-jing WU. Abrasive Wear Behavior and Mechanism of High Chromium Cast Iron[J]. Chinese Journal of Iron and Steel, 2015, 22(1): 84-90. |
| [3] |
YANG Zi-run,LI Dong-sheng,WANG Lan,WANG Shu-qi,WEI Min-xian. Wear Behavior and Mechanism of Spheroidal Graphite Cast Iron[J]. Chinese Journal of Iron and Steel, 2013, 20(10): 81-86. |
| [4] |
WEI Min-xian,WANG Shu-qi,WANG Lan,CUI Xiang-hong,CHEN Kang-min. Selection of Heat Treatment Process and Wear Mechanism of High Wear Resistant Cast Hot-Forging Die Steel[J]. Chinese Journal of Iron and Steel, 2012, 19(5): 50-57. |
| [5] |
ZHANG Mi��lan;XING Shu��ming;XIN Qiao;XIAO Li��ming;GOU Jun��nian;WU Xia��ling. Abnormal Failure Analysis of H13 Punches in Steel Squeeze Casting Process[J]. Chinese Journal of Iron and Steel, 2008, 15(3): 47-0. |
|
|
|
|
2017, Vol. 24 