| Sintering flue gas desulfurization with different carbon materials modified by microwave irradiation |
| Shan Ren*,Fu-qiang Guo,Qi Zhao,Jie Yang,Lu Yao,Ming Kong |
| College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China |
|
|
|
|
Abstract Modification of metallurgical coke, biomass char and semi-coke was carried out using a microwave device with power of 450-850 W and irradiation time of 6-12 min. The desulfurization rates of three carbon materials before and after modification were tested. The effects of microwave power and irradiation time on the pore texture and surface chemical characteristics of the three carbon materials were examined by SEM, BET and Fourier transform infrared spectroscopy (FTIR). The results showed that the specific surface area, total pore volume and pore diameter of biomass char and semi-coke after irradiation decreased slightly. Noteworthily, the pore diameter turned small and the acidic functional groups on their surface decomposed, thereby the basicity of carbon surface increased by microwave modification. The optimal promotion of desulfurization rate of three carbon materials was semi-coke irradiated at 850 W for 9 min and the sulfur dioxide adsorption rate was up to 45%.
|
|
Received: 14 November 2016
Published: 18 October 2017
|
|
|
|
| [1] |
Yong LI,Fu-chun ZHOU,Zhao-xin ZHOU,Zhi-han TIAN,Chao YANG,Xi-ke TIAN. An Innovative Approach to Separate Iron Oxide Concentrate from High-sulfur and Low-grade Pyrite Cinders[J]. Chinese Journal of Iron and Steel, 2016, 23(8): 756-764. |
| [2] |
Jing GUO,Shu-sen CHENG,Zi-jian CHENG,. Characteristics of Deoxidation and Desulfurization during LF Refining Al-killed Steel by Highly Basic and Low Oxidizing Slag[J]. Chinese Journal of Iron and Steel, 2014, 21(2): 166-173. |
| [3] |
Hong-bo YANG,Shu-feng YANG,Jing-she LI,Jiang-shan ZHANG. A Mathematical Model to Characterize RH Desulfurization Process[J]. Chinese Journal of Iron and Steel, 2014, 21(11): 995-1001. |
| [4] |
ZHANG Feng,LI Guang-qiang. Control of Ultra Low Titanium in Ultra Low Carbon Al-Si Killed Steel[J]. Chinese Journal of Iron and Steel, 2013, 20(4): 20-25. |
| [5] |
LIU Yan,ZHANG Zi-mu,LIU Jian-nan,ZHANG Jun-hua,Masamichi Sano,ZHANG Jun. Cold Model Study on Mg Desulfurization of Hot Metal Under Mechanical Stirring[J]. Chinese Journal of Iron and Steel, 2013, 20(12): 1-6. |
| [6] |
CHEN Shu-hao,,WANG Xin-hua,HE Xiao-fei,WANG Wan-jun,JIANG Min. Industrial Application of Desulfurization Using Low Basicity Refining Slag in Tire Cord Steel[J]. Chinese Journal of Iron and Steel, 2013, 20(1): 26-33. |
|
|
|
|
2017, Vol. 24 