Zr55.8Al19.4(Co12xCux)24.8 (x = 0�C0.8 at.%) bulk metallic glasses for surgical devices applications |
Kai-ming Han1 . Jian-bing Qiang1 . Ying-min Wang1 . Bing-bing Zhao2 .PeterHa��ussler3 |
1 Key Laboratory of Materials Modification by Laser, Ion, and Electron Beams Ministry of Education, Dalian University of Technology, Dalian 116024, Liaoning, China 2 ArcX Coating Hub Asia, Hoganas China Co., Ltd.,Shanghai 201799, China 3 Physics Institute, Chemnitz University of Technology,09107 Chemnitz, Germany |
|
|
Abstract Abstract: Zr�CAl�CCo�CCu bulk metallic glasses (BMGs) are promising surgical materials. By using the electron concentration criterion for BMG composition design, a series of Zr55.8Al19.4(Co1-xCux)24.8 (x = 0�C0.8 at.%) alloys were produced, of which BMG rod samples with different diameters were made by copper mold casting. Among these alloys, the Zr55.8Al19.4Co17.36Cu7.44 BMG exhibited a centimeter-scale glass formation size (dmax = 12 mm), an ultrahigh strength (ry = 2.04 GPa), a large room-temperature plasticity (ep = 4.0%), and a fracture toughness (KQ = 120 MPa m1/2), as well as good corrosion resistance in phosphate-buffered solution. The attainment of the combination of properties as large glass-forming ability with excellent mechanical and corrosion stability would suit the surgical devices applications.
|
Received: 06 December 2017
Published: 23 October 2018
|
|
|
|
[1] |
Ashby MF, Greer AL.Metallic glasses as structural materials[J].Scr Mater, Scr Mater, 54:321-326
|
[2] |
Scully JR, Gebert A, Payer JH.Corrosion and related mechanical properties of bulk metallic glasses[J].J Mater Res, 2007, 22:302-313
|
[3] |
Li F, Zheng YF.Recent advances in bulk metallic glasses for biomedical applications[J].Acta Biomater, 2016, 36:1-20
|
[4] |
Meagher P, OCearbhaill ED, Byrne JH, Browne DJ .Bulk metallic glasses for implantable medical devices and surgical tools[J].Adv Mater, 2016, 28:5755-5762
|
[5] |
Dambatta S, Izman S, Yahaya B, Lim JY, Kurniawan D .Mg-based bulk metallic glasses for biodegradable implant materials: A review on glass forming ability, mechanical properties, and biocompatibility[J].J Non-Crystal Solids, 2015, 426:110-115
|
[6] |
Liu L, Qiu CL, Chen Q, Chan KC, Zhang SM .Deformation behavior, corrosion resistance, and cytotoxicity of Ni-free Zr-based bulk metallic glasses[J].J Biomed Mater Res, 2008, 86A:160-169
|
[7] |
Qiu L, Chen Q, Liu L, Chan KC, Zhou JX, Chen PP, Zhang SM .A novel Ni-free Zr-based bulk metallic glass with enhanced plasticity and good biocompatibility[J].Scr Mater, 2006, 55:605-608
|
[8] |
Haeussler P.Interrelations between atomic and electronic structures-liquid and amorphous metals as model systems[J].Phys Rep, 1992, 222:65-143
|
[9] |
Yokoyama Y, Fredriksson H, Yasuda H, Nishijima M, Inoue A.Glassy solidification criterion of Zr50Cu40Al10 alloy[J].Mater Trans, 2007, 48:1363-1372
|
[10] |
Li YH, Zhang W, Dong C, Qiang JB, Xie GQ, Fujita K, Inoue A.Glass-forming ability and corrosion resistance of Zr-based Zr�CNi�CAl bulk metallic glasses[J].J Alloys Compd, 2012, 536:S117-S121
|
[11] |
Wada T, Qin FX, Wang XM, Yoshimura M, Inoue A .Formation and bioactivation of Zr-Al-Co bulk metallic glasses[J].J Mater Res, 2011, 24:2941-2948
|
[12] |
Inoue A, Zhang T .Fabrication of bulk glassy Zr55Al10Ni5Cu30 alloy of 30 mm in diameter by a suction casting method[J].Mater Trans, JIM, 1996, 37:185-187
|
[13] |
Zhang QS, Zhang W, Inoue A .Ni-free Zr-Fe-Al-Cu bulk metallic glasses with high glass-forming ability[J].Scr Mater, 2009, 61:241-244
|
[14] |
Jiang QK, Nie XP, Li YG, Jin Y, Chang ZY, Huang XM, Jiang JZ .Ni-free Zr-based bulk metallic glasses with critical diameter above 20 mm[J].J Alloys Compd, 2007, 443:191-194
|
[15] |
Han KM, Qiang JB, Wang YM, Haeussler P.Zr-Al-Co-Cu bulk metallic glasses for biomedical devices applications[J].J Alloys Compd, 2017, 729:144-149
|
[16] |
Peker A, Johnson WL .A highly processable metallic glass: Zr41.2Ti13.8Cu12.5Ni10.0Be22.5[J].Appl Phys Lett, 1993, 63:2342-2344
|
[17] |
Wada T, Zhang T, Inoue A .Formation and high mechanical strength of bulk glassy alloys in Zr-Al-Co-Cu system[J].Mater Trans, 2003, 44:1839-1844
|
[18] |
Wang YM, Zhang XF, Qiang JB, Wang Q, Wang DH, Li DJ, Shek CH, Dong C.Composition optimization of the Al-Co-Zr bulk metallic glasses[J].Scr Mater, 2004, 50:829-833
|
[19] |
Wang YM, Qiang JB, Wong CH, Shek CH, Dong C .Composition rule of bulk metallic glasses and quasicrystals using electron concentration criterion[J].J. Mater. Res, 2003, 18:642-648
|
[20] |
Liu YH, Wang G, Wang RJ, Zhao DQ, Pan MX, Wang WH.Super plastic bulk metallic glasses at room temperature[J].Science, 2007, 315:1385-1388
|
[21] |
Liu ZQ, Qu RT, Zhang ZF .Elasticity dominates strength and failure in metallic glasses[J].J Appl Phys, 2015, 117:014901-
|
[22] |
Johnson WL, Samwer K.A universal criterion for plastic yielding of metallic glasses with a (T/Tg)2/3 temperature dependence[J].Phys Rev Lett, 2005, 95:195501-
|
[23] |
Cui X, Zu FQ, Jiang WX, Wang LF, Wang ZZ.Achieving superior glass forming ability of Zr-Cu-Al-Ni-Ti/Ag bulk metallic glasses by element substitution[J].J Non-Cryst Solids, 2013, 375:83-87
|
[24] |
Park JM, Han JH, Mattern N, Kim DH, Eckert J.Designing Zr-Cu-Co-Al bulk metallic glasses with phase separation mediated plasticity[J].Metall Mater Trans A, 2012, 43:2598-2603
|
[25] |
Lewandowski JJ, Wang WH, Greer AL.Intrinsic plasticity or brittleness of metallic glasses[J].Phil Mag Lett, 2005, 85:77-87
|
[26] |
Sun BA, Wang WH.The fracture of bulk metallic glasses[J].Prog Mater Sci, 2015, 74:211-307
|
[27] |
Tada H, Paris PC, Irwin GR.The stress analysis of cracks handbook. Hellertown, PA: Del Research Corporation[J]., 1973, :-
|
[28] |
Niinomi M.Mechanical properties of biomedical titanium alloys[J].Mater Sci Eng A, 1998, 243:231-236
|
[29] |
Mizutani U.Electronic structure of metallic glasses[J].Prog Mater Sci, 1983, 28:97-228
|
[1] |
Jun Jiang,. Hua Ding . Zong-an Luo . Guang-ming Xie. Interfacial microstructure and mechanical properties of stainless steel clad plate prepared by vacuum hot rolling[J]. , 2018, 25(7): 732-738. |
[2] |
Zhi-kai Gao, . An-ding Wang,, . Ping-bo Chen . Cheng-liang Zhao, . Fu-shan Li . Ai-na He, . Chun-tao Chang, . Xin-min Wang, . Chain-tsuan Liu. Asynchronous responses of mechanical and magnetic properties to structure relaxation for FeNbB bulk metallic glass[J]. , 2018, 25(6): 637-643. |
[3] |
M.L. Li, ? H. Jiang, ? Y.L. He, ? L.B. Chen, ? G.T. Zhang ? H. Wang ? X.G. Lu, ? L. Li,. Effect of two-step cooling process on mechanical properties of TRIP steel with high performance[J]. , 2018, 25(4): 426-432. |
[4] |
Yi Xiong,? Tian-tian He ? Yan Lu ? Han-sheng Bao ? Yong Li ? Feng-zhang Ren, ? Wei Cao,5 ? Alex A. Volinsky6. Impacts of multiple laser shock processing on microstructure and mechanical property of high-carbon steel[J]. , 2018, 25(4): 469-475. |
[5] |
Jin-ru Luo Xiao Song Mao-yin Wang. Effects of different types of twinning on microstructure and mechanical properties of a strongly textured TA2 commercially pure titanium alloy subjected to rolling at ambient and cryogenic temperatures[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2018, 25(3): 275-281. |
[6] |
Chen Dong, �� Ai-min Zhao, �� Xi-tao Wang �� Qi-hang Pang �� Hui-bin Wu,. Microstructure and properties of 1100 MPa grade low-carbon hot-rolled steel by laser welding[J]. , 2018, 25(2): 228-234. |
|
|
|
|