Effects of Ti addition on corrosion behavior of Zr-based metallic glass in chloride medium |
Zhang-wei-jia Qiu1,2 . Hua-meng Fu2,3 . Hong-wei Zhang2,4 . Hong Li2 . Zheng-kun Li2 . Long Zhang2 . Zheng-wang Zhu2 . Ai-min Wang2 . Hai-feng Zhang2 |
1 School of Materials Science and Engineering, University of Science and Technology of China, Shenyang 110016, Liaoning, China 2 Shenyang National Laboratory for Material Science, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, Liaoning, China 3 Dongguan Eontec Co., Ltd., Dongguan 523662, Guangdong, China 4 Liaoning Jinyan Liquid Metal Technology Co., Ltd.,Shenyang 110100, Liaoning, China |
|
|
Abstract To improve the corrosion resistance of Zr51.3Al10Ni6Cu31.8Ag0.1Y0.8 metallic glass in acid chloride solution, Ti was added into the alloy. XRD results show these Ti-added alloys with diameters of 3 mm are all metallic glasses. Weight loss and electrochemical method were introduced to characterize their corrosion resistance. Results show that the corrosion resistance of metallic glass is significantly improved with Ti addition. XPS study demonstrates that Zr dioxides dominate in passive film during corrosion when Ti content is low. High-content Ti addition can lead to an evident accumulation of Ti dioxides, this accumulation results in a thicker, Ti-enriched protective passive film.
|
Received: 05 December 2017
Published: 23 October 2018
|
|
|
|
|
|
|