| Growth behavior of spinel in stainless steel slag during cooling process |
| Long-hu Cao 1,2 . Cheng-jun Liu 1,2 . Qing Zhao 1,2 . Mao-fa Jiang 1,2 |
1 Key Laboratory for Ecological Metallurgy of Multimetallic Ores Ministry of Education, Northeastern University, Shenyang 110819, Liaoning, China
2 School of Metallurgy, Northeastern University, Shenyang 110819, Liaoning, China |
|
|
|
|
Abstract Spinel is an appropriate phase for sequestrating chromium in stainless steel slag to prevent chromium from polluting, and the crystal size of spinel has a significant effect on the stability of chromium and the extraction efficiency of spinel. The enrichment behavior of chromium in spinel during cooling process was investigated, and the growth process of spinel was studied based on the crystal size distribution theory. The results showed that the enrichment degree of chromium in spinel increased from 88.5% to nearly 100% during the cooling process from 1773 to 1573 K at a rate of 5 K/min. The mean diameter of spinel in stainless steel slag had an obvious growth in the cooling process, and a rapid growth of spinel occurred during the cooling process from 1623 to 1523 K. Leaching results indicated that the leaching amount of chromium could reduce to less than 0.01 mg/L by controlling the cooling condition. The growth mechanism of spinel was investigated and proposed to consist of two stages: in the first stage, the spinel was in the surface-controlled growth with a decaying nucleation rate from 1773 to 1573 K, and in the second stage, the growth mechanism was transformed to supply-controlled Ostwald ripening below 1573 K.
|
|
Received: 28 August 2017
Published: 07 January 2019
|
|
|
|
| Cite this article: |
|
CAO Long-Hu,LIU Zhang-Jun,DIAO Jing, et al. Growth behavior of spinel in stainless steel slag during cooling process[J]. Journal of Iron and Steel Research International, 2018, 25(11): 1131-1139.
|
|
|
|
| 1. |
H. Zhang, H. Xin, Resour. Conserv. Recy. 55(2011)745-754.2. S. Mostafaee, M. Andersson, P. G. J?nsson, Ironmak. Steelmak. 38(2011)90-100.3. R. B. Zhu, G. J. Ma, Y. S. Cai, Y. X. Chen, T. Yang, B. Y. Duan, Z. L. Xue, J. air. Waste. Manage. 66(2016) 402-411.4. H. Shen, E. Forssberg, U. Nordstr?m, Resour. Conserv. Recy. 40(2004)245-271.5. E. Kim, J. Spooren, K. Broos, L Horckmans, M. Quaghebeur, K. C. Vrancken, Hydrometallurgy. 58(2015)139-148.6. B. Dhal, H. N. Thatoi, N. N. Das, B. D. Pandey, J. Hazard. Mater. 251(2013)272-291.7. F. Engstrom, D. Adolfsson, Q. Yang, C. Samuelsson, B. Bjokman, Steel. Res. Int. 81(2010)362-371.8. E. Kim, J. Spooren, K. Broos, P. Nieslen, L. Horckmans, M. Quaghebeur, Chem. Eng. J. 295(2016)542-551.9. Q. Zhao, C. J. Liu, P. Y. Shi, B. Zhang, M. Jiang, Int. Journal. Miner. Process. 130(2014)95-101.10. Q. Zhao, C. J. Liu, B. Zhang, M. F Jiang, J. Qi, H. Saxén, R. Zevenhoven, Steel. Res. Int. 86(2015)1541-1547.11. Y. Dong, X. Wu, L. Li, ISIJ Int. 45(2005)1238-1242.12. X. Wu, L. Li, Y. Dong, ISIJ Int. 47(2007)402-407.13. J. Li, Z. Zhang, L. Liu, W. Wang, X. Wang, ISIJ Int. 53(2013)1696-1703.14. Y. Sun, Z. Li, L. Liu, X. Wang, Z. Zhang, ISIJ Int., 55(2015)158-165.15. H. Cabrera-Real, A. Romero-Serrano, B. Zeifert, A. Hernandez-Ramirez, M. Hallen-López, J. Mater. Cycles. Waste. 14(2012)317-324.16. E. García-Ramos, A. Romero-Serrano, B. Zeifert, P Flores-Sánchez, M. Hallen-López, E. G. Palacios, Steel. Res. Int. 79(2008)332-339.17. Q. F. Shu, Q. Y. Luo, L. J. Wang, K Chou, Steel. Res. Int. 86(2014)391-399.18. J. L. Li, A. J. Xu, D. F. He, Q. X. Yang, N. Y. Tian, Int. J. Min. Met. Mater. 20(2013)253-258.19. L. H. Cao, C. J. Liu, Q. Zhao, M. F. Jiang, J. Iron. Steel. Res. Int. 24(2017)258-265.20. P. Drissen, A. Ehrenberg, D. Mudersbach, M. Dirk, Steel Res. Int. 80(2009)737-745.21. W. Zhou, B. Xie, W. F. Tan, J. Diao, X. Zhang, H. Y. Li, JOM. 68(2016)1-5.22. X. Zhang, B. Xie, J. Diao, X. J. Li, Ironmak. Steelmak. 39(2012)147-154.23. D. Turnbull, J. Appl. Phys., 21(1950)1022-10258.24. C. Brime, D. D. Eberl, Schwiez. Mineral. Petrogr. Mitt. 82(2002)203-209.25. R. C. F. Lentze, H. Y. M. Jr, Meteorit Planet. Sci. 35(2010)919-927.26. A. Torkian, N. Salehi, M. Kord, Petrology. 4(2013)33-46.27. H. Pourkhors, I. H. Mirnejad, D Raiesi, J. Hassanzadeh, GeolCarpath. 66(2015)257-268.28. H. M. Yu, J. D. Xu, C. Lin, L. Shi, X. D. Chen, J. Asian. Earth. Sci. 58(2012)1-15.29. D. J. Bove, D. D. Eberl, D. K. McCarty, G. P. Meeker, Am. Miner. 87(2002)1546-1556.30. D. R. Uhlmann, J. Non-Cryst. Solids. 7(1972)337-348.31. D. Turnbull, J. Appl. Phys. 21(1950)1022-1028.32. D. D. Eberl, V. A. Dirts, J. Srodon, Am. J. Sci. 298(1998)499-533.33. J. Diao, W. Zhou, B. Xie, Crystengcomm. 18(2016)6272-6281.34. L. S. Li, X. R. Wu, L. Yu, Y. C. Dong, Ironmak. Steelmak. 35(2008)367-370.35. X. R. Wu, L.S. Li, Y. C. Dong, ISIJ Int. 47(2007)402-407.36. G. M. Yang, X. R. Wu, L. S. Li, Z. J. Wu, F. B. Cao, Can. Metall. Quart. 51(2012)150-156.
|
| [1] |
Shuang-qin Chen . Liang-zhengDong . Ke-zhen Hui . Zhen Peng . Zhun Li . Zhi-Chao Lu . Yang Shao . Ke-fu Yao. Fe-based multi-phase nanocrystalline ribbons with hierarchically flowerlike structured metal oxides after modified by Orange II for CrVI absorption[J]. , 2018, 25(6): 608-613. |
| [2] |
Jae-hong Shin · Joo-hyun Park . Effect of CaF2 content in refining slag on formation behavior of spinel inclusion in Ni–Cr–V-alloyed special steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2018, 25(2): 157-163. |
| [3] |
Long-hu Cao,Cheng-jun Liu*,Qing Zhao,Mao-fa Jiang. Effect of Al2O3 modification on enrichment and stabilization of chromium in stainless steel slag[J]. Chinese Journal of Iron and Steel, 2017, 24(3): 258-265. |
| [4] |
Hai-feng Xu,,*,Feng Yu,Chang Wang,Wan-li Zhang,Jian Li,Wen-quan Cao. Comparison of microstructure and property of high chromium bearing steel with and without nitrogen addition[J]. Chinese Journal of Iron and Steel, 2017, 24(2): 206-213. |
| [5] |
Dongping ZHAN,Yangpeng ZHANG,Zhouhua JIANG,Dewei WANG,Huishu ZHANG. Chromium Recycling from Argonoxygen Decarburization Dust in Hot Metal Predephosphorization Process[J]. Chinese Journal of Iron and Steel, 2016, 23(9): 867-873. |
| [6] |
Bao-chao ZHENG,Zhi-fu HUANG,Jian-dong XING,Yi-yang XIAO,Xiao FAN,Yong WANG. Effects of Chromium Addition on Preparation and Properties of Bulk Cementite[J]. Chinese Journal of Iron and Steel, 2016, 23(8): 842-850. |
|
|
|
|
2018, Vol. 25 