Structure–property relationships in heat-affected zone of gas-shielded arc-welded V–N microalloyed steel |
Jun Hu1 . Lin-xiu Du1 . Bin Zhang1 . Xiang-yu Qi1 . Xiu-hua Gao1 . R.D.K. Misra2 |
1 The State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, Liaoning, China 2 Laboratory for Excellence in Advanced Steel Research, Department of Metallurgical, Materials and Biomedical Engineering, University of Texas at El Paso, El Paso, TX 79968-0521, USA |
|
|
Abstract The structure–property relationship in heat-affected zone (HAZ) of a low-carbon steel bearing V–N subjected to gasshielded arc welding was explored. The microstructural characteristics of base metal (BM), coarse-grained HAZ (CGHAZ), fine-grained HAZ, and intercritical HAZ were significantly different. The effect of grain-refinement strengthening and transformation hardening on HAZ contributed to equivalent hardness of 260.8–278.5 HV in comparison with BM hardness of 272.0 HV. Moreover, excellent impact toughness at - 20 °C was obtained because of high resistance to crack propagation by high-misorientation boundaries, leading to impact fracture consisting of dimples. In CGHAZ, free N was partly fixed by V(C, N) precipitates, such that the deterioration effect of N on toughness was considered to be nearly eliminated. In comparison with CGHAZ, weld metal contained higher fraction of acicular ferrite with fine plates, while the impact toughness was inferior because of the detrimental influence of coarse inclusions from the welding wire. The nanoscale V(C, N) precipitates in CGHAZ had weak effect on toughness because of small size.
|
Received: 17 October 2017
Published: 23 January 2019
|
|
|
|
Cite this article: |
HU Jun,DU Lin-Xiu,ZHANG Ban, et al. Structure–property relationships in heat-affected zone of gas-shielded arc-welded V–N microalloyed steel[J]. Journal of Iron and Steel Research International, 2018, 25(12): 1244-1254.
|
|
|
|
[1] |
R.D.K. Misra, H. Nathani, J.E. Hartmann and F. Siciliano: Mater. Sci. Eng. A, 394 (2005), 339-352.
|
[2] |
C.L. Davis and J.E. King: Metall. Mater. Trans. A, 25 (1994), 563-573.
|
[3] |
X.H. Yu, J.L. Caron, S.S. Babu, J.C. Lippold, D. Isheim and D.N. Seidman: Acta Mater., 58 (2010), 5596-5609.
|
[4] |
R. Lagneborg, T. Siwecki, S. Zajac and B. Hutchinson: Scand. J. Metall., 28 (1999), 186-241.
|
[5] |
T. Senuma: ISIJ Int., 42 (2002), 1-12.
|
[6] |
J. Hu, L.X. Du, J.J. Wang, H. Xie, C.R. Gao and R.D.K. Misra: Mater. Sci. Eng. A, 585 (2013), 197-204.
|
[7] |
J. Hu, L.X. Du, H. Xie, X.H. Gao and R.D.K. Misra: Mater. Sci. Eng. A, 607 (2014), 122-131.
|
[8] |
H.W. Yen, C.Y. Chen, T.Y. Wang, C.Y. Huang and J.R. Yang: Mater. Sci. Technol., 26 (2010), 421-430.
|
[9] |
S.H. Zhang, N. Hattori, M. Enomoto and T. Tarui: ISIJ Int., 36 (1996), 1301-1309.
|
[10] |
J. Hu, L.X. Du, M. Zang, S.J. Yin, Y.G. Wang, X.Y. Qi, X.H. Gao and R.D.K. Misra: Mater. Charact., 118 (2016), 446-453.
|
[11] |
J. Hu, L.X. Du and J.J. Wang: Scr. Mater., 68 (2013), 953-956.
|
[12] |
A.E. Amer, M.Y. Koo, K.H. Lee, S.H. Kim and S.H. Hong: J. Mater. Sci., 45 (2010), 1248-1254.
|
[13] |
L.Y. Lan, C.L. Qiu, D.W. Zhao, X.H. Gao and L.X. Du: J. Mater. Sci., 47 (2012), 4732-4742.
|
[14] |
ISO 9692-2, Welding and allied processes-Joint preparation-Part 2: Submerged arc welding of steels (1998).
|
[15] |
ISO 6507-1, Metallic materials-Vickers hardness test-Part 1: Test method (2005).
|
[16] |
ISO 9016, Destructive tests on welds in metallic materials-impact tests-test specimen location, notch orientation and examination (2001).
|
[17] |
Annual Book of ASTM Standards, ASTM Designation, E8 and E23, vol. 03.01, Philadelphia, PA, (1995) p. 142.
|
[18] |
L. Tan, K. Sridharan, T.R. Allen, R.K. Nanstad and D.A. McClintock: J. Nucl. Mater., 374 (2008), 270-280.
|
[19] |
Y. You, C. Shang, L. Chen and S. Subramanian: Mater. Sci. Eng. A, 546 (2012), 111-118.
|
[20] |
Y. You, C. Shang, L. Chen and S. Subramanian: Mater. Des., 43 (2013), 485-491.
|
[21] |
L.Y. Lan, C.L. Qiu, D.W. Zhao, X.H. Gao and L.X. Du: Mater. Sci. Eng. A, 529 (2011), 192-200.
|
[22] |
Y.M. Kim, H. Lee and N.J. Kim: Mater. Sci. Eng. A, 478 (2008), 361-370.
|
[23] |
R.A. Ricks, P.R. Howell and G.S. Barritte: J. Mater. Sci., 17 (1982), 732-740.
|
[24] |
A.R. Mills, G. Thewlis and J.A. Whiteman: Mater. Sci. Technol., 3 (1987), 1051-1061.
|
[25] |
J.R. Yang and H.K.D.H. Bhadeshia: J. Mater. Sci., 26 (1991), 839-845.
|
[26] |
T.K. Lee, H.J. Kim, B.Y. Kang and S.K. Hwang: ISIJ Int., 40 (2000), 1260-1268.
|
[27] |
J.H. Shim, Y.W. Cho, S.H. Chung, J.D. Shim and D.N. Lee: Acta Mater., 47 (1999), 2751-2760.
|
[28] |
K.F.A. Hajeri, C.I. Garcia, M. Hua and A.J. Deardo: ISIJ Int., 46 (2006), 1233-1240.
|
[29] |
D.V. Edmonds and R.C. Cochrane: Metall. Trans. A, 21 (1990), 1527-1540.
|
[30] |
A.D. Schino and C. Guarnaschelli: Mater. Lett., 63 (2009), 1968-1972.
|
[31] |
J. Nohava, P. Hausild, M. Karlik and P. Bompard: Mater. Charact., 49 (2002), 211-217.
|
[32] |
B. Cui, Y. Peng, L. Zhao, M. Peng, T. An and C. Ma: ISIJ Int., 56 (2016), 132-139.
|
[33] |
Z. Guo, C.S. Lee and J.W. Morris: Acta Mater., 52 (2004), 5511-5518.
|
[34] |
T. Ohmura, A.M. Minor, E.A. Stach and J.W. Morris: Mater. Res., 19 (2004), 3626-3632.
|
[35] |
J.W. Morris, C.S. Lee and Z. Guo: ISIJ Int., 43 (2003), 410-419.
|
[36] |
D.A. Curry and J.F. Knott: Met. Sci., 13 (1979), 341-345.
|
[37] |
S. Maropoulos and N. Ridley: Mater. Sci. Eng. A, 384 (2004), 64-69.
|
[1] |
Hai-zhong Zheng, Sheng-hua Guo, Qin-hao Luo, Xiao-yong Shu, Gui-fa Li. Effect of shot peening on microstructure, nanocrystallization and microhardness of Ti–10V–2Fe–3Al alloy surface[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(1): 52-58. |
[2] |
Qi Zhou, Zhuang Li, Zhan-shan Wei, Di Wu, Jin-yu Li, Zhen-yao Shao. Microstructural features and precipitation behavior of Ti, Nb and V microalloyed steel during isothermal processing[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(1): 102-111. |
[3] |
Hai-feng Xu . Gui-lin Wu . Chang Wang . Jian Li . Wen-quan Cao. Microstructure, hardness and contact fatigue properties of X30N high nitrogen stainless bearing steel[J]. , 2018, 25(9): 954-967. |
[4] |
Zhen Li . Dong-hui Wen . Yue Ma . Qing Wang . Guo-qing Chen . Rui-qian Zhang . Rui Tang . Huan He. Prediction of alloy composition and microhardness by random forest in maraging stainless steels based on a cluster formula[J]. , 2018, 25(7): 717-723. |
[5] |
Long-yun Xu, ? Jian Yang ? Rui-zhi Wang ? Wan-lin Wang ? Yu-nan Wang. Effect of Mg addition on formation of intragranular acicular ferrite in heat-affected zone of steel plate after high-heat-input welding[J]. , 2018, 25(4): 433-441. |
[6] |
Cheng-hui Su · Qiang-guo Li · Xue-fei Huang · Wei-gang Huang. Effect of bainite microstructure during two-step quenching and partitioning process on strength and toughness properties of a 0.3%C bainitic steel[J]. , 2018, 25(2): 235-242. |
|
|
|
|