Effect of precipitates on high-temperature strength and irradiation behavior of vanadium-based alloys |
Shao-ning Jiang1 . Li-qun Xu1 . Fa-rong Wan2 |
1 School of Mechanical and Automotive Engineering, Qilu University of Technology Shandong Academy of Science, Jinan 250353, Shandong, China 2 School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China |
|
|
Abstract The formation of precipitates and their effect on mechanical properties and irradiation damage in V–4Cr–4Ti alloys have been investigated using transmission electron microscope, high-temperature tensile tests and high-voltage electron microscope (HVEM). V–4Cr–4Ti alloys were aged for 20–40 h at 873 K, and extremely fine precipitates were produced during the aging process, which coarsened with aging time. The results of high-temperature (773, 873 and 973 K) tensile tests showed an increase in strength with increasing aging time (i.e., increasing size of precipitates) while a decrease in the uniform elongation. There was evidence that presence of precipitates strengthened V–4Cr–4Ti alloys. In situ HVEM observations showed that the precipitates restricted the growth rate of dislocation loops induced during electron irradiation at 773 K. The interactions between precipitates and irradiation-induced dislocation loops were discussed. The presence of particles alleviated the increase in irradiation hardening up to an irradiation dose of 3.42 dpa (displacement per atom). The precipitates shrank in size during electron irradiation, which was due to the dissolution of constituent atoms of the precipitates into the alloy matrix.
|
Received: 25 January 2018
Published: 23 January 2019
|
|
|
|
Cite this article: |
SHAONING -Jiang. Effect of precipitates on high-temperature strength and irradiation behavior of vanadium-based alloys[J]. Journal of Iron and Steel Research International, 2018, 25(12): 1270-1277.
|
|
|
|
[1] |
YIN Bin, LI Wan-ming, WU Shao-peng, ZANG Xi-min, YU Hao-cen. Thermodynamic analysis of Al and Ti element loss in electroslag remelting Inconel718 superalloy[J]. Iron and Steel, 2019, 54(5): 86-94. |
[2] |
WANG Chun-mei1, LI Zhi-liang2. Method for improving efficiency of cold rolling logistics[J]. Iron and Steel, 2019, 54(5): 95-99. |
[3] |
WANG Xiao-ai1, JIANG Xin2, GAO Yuan3, HUO Hong-yan3, SHEN Feng-man2. Investigation on fluidity of SFCA and sintering strength based on phase diagram[J]. Iron and Steel, 2019, 54(5): 9-13. |
[4] |
ZHANG Lin-lin, FU Gang-hua, GUO Yu-feng, CHEN Feng, ZHENG Fu-qiang . Effect of basicity on quality of green fluxed pellets[J]. Iron and Steel, 2019, 54(5): 14-18. |
[5] |
MA Xiao-gang, CHEN Liang-yu, LI Yang. Calculation of convective heat transfer coefficient of hearth cooling stave and furnace heating transfer characteristics[J]. Iron and Steel, 2019, 54(5): 19-26. |
[6] |
ZHANG Jian-jun1,2, MAO Xin-ping 2, WANG Chun-feng3, ZHU Wan-jun2. Development and expection on high-efficiency producing technology of steelmaking in TSCR line[J]. Iron and Steel, 2019, 54(5): 1-8. |
|
|
|
|