| Creep rupture behavior and microstructural evolution of modified 9Cr–1Mo heat-resistant steel |
| Fa-cai Ren1 . He Wang2 . Xiao-ying Tang1 . Fei Chen3 |
1 Shanghai Institute of Special Equipment Inspection and Technical Research, Shanghai 200062, China
2 Capital Aerospace Machinery Corporation Limited, Beijing 100076, China
3 National Engineering Research Centre of Die & Mold CAD, Shanghai Jiao Tong University, Shanghai 200030, China |
|
|
|
|
Abstract High-temperature creep rupture behavior of modified 9Cr–1Mo steel used for steam cooler was investigated at temperature of 838 and 923 K and stress ranging from 100 to 250 MPa. Based on the analysis of creep rate–time curves, it is found that the creep rupture life decreases with the increase in the applied stress and temperature. The creep damage tolerance factor has been identified as a value of 8. In the normalized and tempered condition, the studied steel shows typical martensitic microstructure with Cr-rich M23C6 and Nb- or V-rich MX precipitates. Moreover, the Laves phase has been found along the grain boundaries. The fracture morphology characterized by field emission scanning electron microscope is adopted to reveal the creep failure mechanisms. The investigated results indicate the occurrence of the transgranular fracture under all the creep test conditions.
|
|
Received: 21 August 2017
Published: 23 January 2019
|
|
|
|
| Cite this article: |
|
REN Fa-Cai,FEI -Chen,TANG Xiao-Yang. Creep rupture behavior and microstructural evolution of modified 9Cr–1Mo heat-resistant steel[J]. Journal of Iron and Steel Research International, 2018, 25(12): 1303-1307.
|
|
|
|
| [1] |
T. Shrestha, M. Basirat, I. Charit, G.P. Potirniche, K.K. Rink. Creep rupture behavior of Grade 91 steel [J]. Materials Science and Engineering A, 2013, 565(5): 382-391.
|
| [2] |
R.L. Klueh. Elevated temperature ferritic and martensitic steels and their application to future nuclear reactors [J]. International Materials Reviews, 2005, 50(5): 287-310.
|
| [3] |
A. Kostka, K.G. Tak, R.J. Hellmig, Y. Estrin, G. Eggeler. On the contribution of carbides and micrograin boundaries to the creep strength of tempered martensite ferritic steels [J]. Acta Materialia, 2007, 55 (2) : 539-550.
|
| [4] |
H. Wang, W. Yan, S. van Zwaag, Q.Q. Shi, W. Wang, K. Yang, Y.Y. Shan. On the 650℃ thermostability of 9-12Cr heat resistant steels containing different precipitates [J]. Acta Materialia, 2017, 134: 143-154.
|
| [5] |
K. Sawada, K. Kubo, F. Abe. Creep behavior and stability of MX precipitates at high temperature in 9Cr-0.5Mo-1.8W-VNb steel [J]. Materials Science and Engineering A, 20013, 19-321(15): 784-787.
|
| [6] |
J. Pesicka, A. Dronhofer, G. Eggeler. Free dislocations and boundary dislocations in tempered martensite ferritic steels [J]. Materials Science and Engineering A, 2004, 387-389: 176-180.
|
| [7] |
Q. Lu, Y. Toda, N. Harada, W. Xu, S. van der Zwaag. The impact of intended service temperature on the optimal composition of Laves and M23C6 precipitate strengthened ferritic creep resistant steels [J]. Computational Materials Science, 2015, 107: 110-115.
|
| [8] |
M. Basirat, T. Shrestha, G.P. Potirniche, I. Charit, K. Rink. A study of the creep behavior of modified 9Cr-1Mo steel using continuum-damage modeling [J]. International Journal of Plasticity, 2012, 37: 95-107.
|
| [9] |
A. Aghajani, F. Richter, C. Somsen, S.G. Fries, I. Steinbach, G. Eggeler. On the formation and growth of Mo-rich Laves phase particles during long-term creep of a 12% chromium tempered martensite ferritic steel [J]. Scripta Materialia, 2009, 61(11): 1068-1071.
|
| [10] |
W. Yan, W. Wang, Y.Y. Shan, K. Yang. Microstructural stability of 9-12%Cr ferrite/martensite heat-resistant steels [J]. Frontiers of Materials Science, 2013, 7(1): 1-27.
|
| [11] |
A. Aghajani, F. Richter, C. Somsen, S.G. Fries, I. Steinbach and G. Eggeler. On the formation and growth of Mo-rich Laves phase particles during long-term creep of a 12% chromium tempered martensite ferritic steel [J]. Scripta Materialia, 2009, 61(11): 1068-1071.
|
| [12] |
Y.P. Zhao, J.M. Gong, J. Yong, X.W. Wang, L.M. Shen, Q.N. Li. Creep behaviours of Cr25Ni35Nb and Cr35Ni45Nb alloys predicted by modified theta method [J]. Materials Science and Engineering A, 2016, 649: 1-8.
|
| [13] |
T. Shrestha, M. Basirat, I. Charit, G.P. Potirniche, K.K. Rink, U. Sahaym. Creep deformation mechanisms in modified 9Cr-1Mo steel [J]. Journal of Nuclear Materials, 2012, 423(1-3): 110-119.
|
| [14] |
P. Anderson, T. Bellgardt, F. L. Jones. Creep deformation in a modified 9Cr-1Mo steel [J]. Materials Science & Technology, 2003, 19(2): 207-213.
|
| [15] |
V. Sklenica, K. Kucharova, A. Dlouhy, J. Krejci. Proceedings of Conference on Materials for Advanced Power Engineering, Liege, Belgium, 1994. p. 435.
|
| [16] |
K. Kimura, H. Kushima, K. Swada. Long-term creep deformation property of modified 9Cr–1Mo steel [J]. Materials Science and Engineering A, 2009, 510-511: 58-63.
|
| [17] |
S. Spigarelli, E. Quadrini. Analysis of the creep behaviour of modified P91 (9Cr–1Mo–NbV) welds [J]. Materials and Design, 2002, 23(6): 547-552.
|
| [18] |
V. Sklenicka, K. Kucharova, M. Svoboda, L. Kloc, J. Bursik, A. Kroupa. Long-term creep behavior of 9-12%Cr power plant steels [J]. Materials Characterization, 2003, 51(1): 35-48.
|
| [19] |
B.K. Choudhary, E. Isaac Samuel. Creep behaviour of modified 9Cr–1Mo ferritic steel [J]. Journal of Nuclear Materials, 2011, 412(1): 82-89.
|
| [20] |
F.C. Monkman, N.J. Grant. Proc. Am. Soc. Test. Mater. 1956, 56: 593.
|
| [21] |
H.E. Evans. Mechanics of creep fracture. Elsevier Applied Science Publishers, New York, NY, 1984: 18–22.
|
| [22] |
F. Dobes, K. Milicka. Met. Sci., 1976, 10: 382-384.
|
| [23] |
S. Spigarelli, E. Cerri, P. Bianchi, E. Evangelista. Interpretation of creep behaviour of a 9Cr–Mo–Nb–V–N (T91) steel using threshold stress concept [J]. Materials Science & Technology, 1999, 15(12): 1433-1440.
|
| [24] |
C.G. Panait, A. Zielinska-Lipiec, T. Koziel, A. Czyrska-Filemonowicz, A.F. Gourgues-Lorenzon, W. Bendick. Evolution of dislocation density, size of subgrains and MX-type precipitates in a P91 steel during creep and during thermal ageing at 600℃ for more than 100,000h [J]. Materials Science and Engineering A, 2010, 527(16-17): 4062–4069.
|
| [25] |
A. Kipelova, R. Kaibyshev, A. Belyakov, D. Molodov. Microstructure evolution in a 3%Co modified P911 heat resistant steel under tempering and creep conditions [J]. Materials Science and Engineering A, 2011, 528(3): 1280-1286.
|
| [26] |
M. Nie, J. Zhang, F. Huang, J.W. Liu, X.K. Zhu, Z.L. Chen, L.Z. Ouyang. Microstructure evolution and life assessment of T92 steel during long-term creep [J]. Journal of Alloys and Compounds, 2014, 588: 348-356.
|
| [27] |
Y.H. Wei, S.F. Qiao, F.G. Lu, W. Liu. Failure transition mechanism in creep rupture of modified casting 9Cr-1.5Mo-1Co welded joint [J]. Materials and Design, 2016, 97: 268-278.
|
| [28] |
M. Yurechko, C. Schroer, O. Wedemeyer, A. Skrypnik, J. Konys. Creep-to-rupture of 9%Cr steel T91 in air and oxygen-controlled lead at 650°C [J]. Journal of Nuclear Materials, 2011, 419(1): 320-328.
|
| [1] |
Mei Xu, Hui Li, Rui-ting Jiang, Di Tang, Hai-tao Jiang, Zhen-li Mi. Deformation behavior and microstructural evolution in ultra-high-strength dual-phase (UHS-DP1000) steel with different strain rates[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(2): 173-181. |
| [2] |
Zhong-liang Tian,,Sen-bao Jiang,Zheng-zong Chen,Han-sheng Bao,Zheng-dong Liu,*. Microstructural evolution and mechanical properties of a new Ni-based heat-resistant alloy during aging at 750°C[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 513-519. |
| [3] |
Jun Tan,*,Jun-yan Gao,Xue-mei Qin,Zheng-rong Fu,Dong Li,Min Li,Xiu-chang Wang, Gang Wang. Fractography and morphology of shear bands of a Zr-based bulk metallic glass[J]. Chinese Journal of Iron and Steel, 2017, 24(4): 385-389. |
| [4] |
Xue-feng Peng,Jing Liu,*,Jing-tao Han,Dong-bin Wei. Effect of hot/warm roll-forming process on microstructural evolution and mechanical properties of local thickened U-rib for orthotropic steel deck[J]. Chinese Journal of Iron and Steel, 2017, 24(3): 335-342. |
| [5] |
Han-bo Jiang,Xi-nan Luo,Xiao-yan Zhong,*,Hui-hua Zhou,Cun-yu Wang,Jie Shi,Han Dong. In-situ microstructural evolutions of 5Mn steel at elevated temperature in a transmission electron microscope[J]. , 2017, 24(11): 1109-1114. |
| [6] |
Fu-ming LIU,Jian-jun WANG,,Yu-jie LIU,R.D.K. MISRA,Chun-ming LIU,. Effects of Nb and V on Microstructural Evolution, Precipitation Behavior and Tensile Properties in Hot-rolled Mo-bearing Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(6): 559-565. |
|
|
|
|
2018, Vol. 25 