| Wear behavior of TC11 and AISI M2 in pin–disk tribo-system |
| Lan Wang 1 , Jing-han Yang 2 , Yang Li 2 , Jie Song 2 , Yun-xue Jin 3 , Shu-qi Wang 1 |
| 1 School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013, Jiangsu, China 2 Jingjiang College, Jiangsu University, Zhenjiang 212013, Jiangsu, China 3 School of Materials Science and Engineering, Jiangsu University of Science and Technology, Zhenjiang 212003, Jiangsu, China |
|
|
|
|
Abstract The wear behavior and mechanism of TC11 (pins) and AISI M2 (disks) under different test conditions were studied. The results show that tribo-layers formed on the worn surfaces of both TC11 alloy and AISI M2 steel. As for TC11 alloys at 25?C, the wear rate increased to high values with an increase in the load; and abrasive wear and adhesive wear prevailed. However, at 600 ?C, the wear rate decreased sharply and oxidative wear prevailed. As for AISI M2 steels, at 25 and 600 ?C, the wear rates were relatively low. The wear mechanisms at 25 and 600 ?C were abrasive wear and oxidative wear, respectively. The wear rates of AISI M2 steel were lower than those of TC11 alloy at 25 and 600 ?C. The wear performance of the tribo-pair was noticed to be closely related to their mutual contact mode except for the test conditions and the pin and disk materials, and the intermittent contact mode reduced wear of AISI M2 steel.
|
|
|
|
|
|
| Cite this article: |
|
Lan Wang,Jing-han Yang,Yang Li, et al. Wear behavior of TC11 and AISI M2 in pin–disk tribo-system[J]. Journal of Iron and Steel Research International, 2019, 26(5): 490-500.
|
|
|
|
| [1] |
De-hong Lu . Hai-zhou Li . Bo Ren. Effect of Si content on impact-abrasive wear resistance of Al2O3p/steel composites prepared by squeeze casting[J]. , 2018, 25(9): 984-994. |
| [2] |
Zhen Cao,Shu-qi Wang*,Ke-zhi Huang,Bo Zhang,Guo-hong Wen,Qiu-yang Zhang,Lan Wang. Effect of artificial tribological layer on sliding wear behavior of H13 steel[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 943-949. |
| [3] |
Xiu-lin JI,Ju-yi WANG,Cui-cui JI,Jian-hua ZHAO. Abrasive Wear Resistance of Dual Phase Steels DP980 and DP600[J]. Chinese Journal of Iron and Steel, 2015, 22(4): 317-323. |
| [4] |
Ting SUN,Ren-bo SONG,Xu WANG,Peng DENG,Chun-jing WU. Abrasive Wear Behavior and Mechanism of High Chromium Cast Iron[J]. Chinese Journal of Iron and Steel, 2015, 22(1): 84-90. |
| [5] |
YANG Zi-run,LI Dong-sheng,WANG Lan,WANG Shu-qi,WEI Min-xian. Wear Behavior and Mechanism of Spheroidal Graphite Cast Iron[J]. Chinese Journal of Iron and Steel, 2013, 20(10): 81-86. |
| [6] |
Karin Gong,LUO He-li,ZHOU Zhi-feng,TIAN Zhi-ling,Lars Nyborg,LI Chang-hai. Wear Evaluation on Ni3Al/MnS Composite Related to Metallurgical Processes[J]. Chinese Journal of Iron and Steel, 2012, 19(7): 46-54. |
|
|
|
|
2019, Vol. 26 