Effect of Nb on corrosion behavior of inner bottom plate of cargo oil tankers |
Xiang-yu Xu1 Long Tian2 Yun Zhou3 Ming-yu Sun1 Xue-min Wang1 Cheng-jia Shang1 R.D.K. Misra4 |
1 Collaborative Innovation Center of Steel Technology, University of Science and Technology Beijing, Beijing 100083, China; 2 Tianjin Long March Launch Vehicle Manufacturing Co., Ltd., Tianjin 300462, China; 3 Institute of Research of Iron and Steel (IRIS), Sha-steel, Zhangjiagang 215625, Jiangsu, China; 4 Center for Structural and Functional Materials Research and Innovation, Department of Metallurgical and Materials Engineering, University of Texas at E1 Paso, E1 Paso, TX 79968, USA |
|
|
Abstract The effect of Nb on the corrosion resistance of steels in simulating an oil-corrosion environment was investigated by means of microstructure observation, electrochemical test, dissolved Nb content measurement and Nb segregation observation. The results show that the microstructure of the experimental steels is mainly ferrite with a little pearlite. The dissolved Nb contents of the experimental steels are 0.0235 and 0.0458 wt.%, respectively, while the undissolved Nb content is nearly the same. In addition to enhancing mechanical properties of the steel, dissolved Nb improves the corrosion resistance by enriching Nb in the rust layer. Nb oxides in the rust layer cause a decrease in the corrosion rate due to a decrease in the anodic reaction kinetics. The segregation of Nb at the grain boundaries suppresses the corrosion. Moreover, Nb is enriched at the bottom of the corrosion pit and prevents any further corrosion.
|
|
|
|
|
Cite this article: |
Xiang-yu Xu,Long Tian,Yun Zhou, et al. Effect of Nb on corrosion behavior of inner bottom plate of cargo oil tankers[J]. Journal of Iron and Steel Research International, 2019, 26(6): 611-620.
|
|
|
|
[1] |
Xiao-wei Feng, Juan Xie, Wen-ying Xue, Yong-feng Shen, Hong-bo Wang, Zhen-yu Liu. Microstructure and nanoindentation hardness of shot-peened ultrafine-grained low-alloy steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(5): 472-482. |
[2] |
Shang-lin Lv . Zhong-min Yang . Bin Zhang, . Jie Chen . Ying Chen . Xiao-bin Li. Corrosion passive behaviour duplexstainlesssteelat different rates simulated marine-environmentsolution[J]. , 2018, 25(9): 943-953. |
[3] |
Emna Ben Fredj Hadi Ghasemi Nanesa Mohammad Jahazi Jean-Benoit Morin. Influence of initial microstructure and grain size on transformation of bainite to austenite in large size forgings[J]. , 2018, 25(5): 554-562. |
[4] |
Ebrahim Mortazavi,Reza Amini Najafabadi,Amirhossein Meysami*. Effect of heat input on microstructure and mechanical properties of dissimilar joints of AISI 316L steel and API X70 high-strength low-alloy steel[J]. , 2017, 24(12): 1248-1253. |
[5] |
Liang HE,,Yan- jun GUO,Xia- yu WU,Yi- ming JIANG,Jin LI. Effect of Solution Annealing Temperature on Pitting Behavior of Duplex Stainless Steel 2204 in Chloride Solutions[J]. Chinese Journal of Iron and Steel, 2016, 23(4): 357-363. |
[6] |
Li-cong AN,Jing CAO,Lin-cai WU,Hong-huan MAO,Yi-tao YANG. Effects of Mo and Mn on Pitting Behavior of Duplex Stainless Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(12): 1333-1341. |
|
|
|
|