| Influence of coating and dew point on hearth roll pickup |
| Xiao-fei Zheng1,2 Yong-lin Kang1 Jian Zhou2 |
| 1 School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China; 2 Shougang Jingtang Iron and Steel United Co., Ltd., Tangshan 063200, Hebei, China |
|
|
|
|
Abstract Thermal spray coatings have been widely used on hearth rolls in a continuous annealing line to improve steel sheet quality and prolong the roll service life. One of the common defects formed on a working hearth roll is the oxide pickup. The most common cause of the pickup formation is that the active Mn oxide reacts with coating. The potentials of two different coatings, CoCrAlYTa–Al2O3 (No. 1) and CoCrYNi–Y2O3 (No. 2), to duplicate pickups by reacting with Fe and Mn oxides were studied. There are three stages during pickup producing and growing. No. 2 coating effectively reduced the corrosion of Mn oxide. The characterization and modification of the surface oxide formed can be changed with different dew points. The results indicate that the dew point from - 53 to - 10 C can change the depth of Mn oxide, such that an alteration can prevent the first stage and second stage and is good for preventing the pickup growing.
|
|
|
|
|
|
| Cite this article: |
|
Xiao-fei Zheng,Yong-lin Kang,Jian Zhou. Influence of coating and dew point on hearth roll pickup[J]. Journal of Iron and Steel Research International, 2019, 26(6): 647-652.
|
|
|
|
| [1] |
Zhang-fu Yuan, Shan-shan Xie, Xiang-tao Yu, Jian Liu, Ping Du, Zhi-hua Li. Wear-resistant coating spraying technique for wear-proofing cover of coke dry quenching furnace[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(2): 123-129. |
| [2] |
Shan-shan Liu, Hai-yan Chen, Xuan Zhao, Li Fan, Xiao-ming Guo, Yan-sheng Yin. Corrosion behavior of Ni-based coating containing spherical tungsten carbides in hydrochloric acid solution[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(2): 191-199. |
| [3] |
Xiao-juan Pang, Shu-suo Li, Lu Qin, Yan-ling Pei, Sheng-kai Gong. Effect of trace Ce on high-temperature oxidation behavior of an Al–Si-coated Ni-based single crystal[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(1): 78-73. |
| [4] |
Ping-hu Chen, · Zhi-lin Liu, · Rui-qing Li, · Chang-jun Qiu · Xiao-qian Li,,. Thermal-sprayed coating of optimally mixed ceramic powders on stainless steel with enhanced corrosion resistance[J]. , 2018, 25(2): 207-212. |
| [5] |
Luis Daniel Aguilera Camacho,Santos García Miranda,Karla Judith Moreno. Tribological performance of uncoated and TiCN-coated D2, M2 and M4 steels under lubricated condition[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 823-829. |
| [6] |
Jun-feng Zhao,Shan-guang Liu,Xiao-guang Yuan,*,Jian-fei Sun,**,Hong-jun Huang, Fu-yang Cao,Hong-xian Shen,Yu-long Wang. Effect of Al22Si/ZL102 bimetal interface fabricated by extrusion at near-eutectic temperature[J]. Chinese Journal of Iron and Steel, 2017, 24(4): 469-474. |
|
|
|
|
2019, Vol. 26 