| Comprehensive evaluation of sintering basic characteristics of iron ore based on grey relational analysis |
| Dong-hui Liu1, Jun-hua Li1, Yue Peng1, Jian-liang Zhang2, Guang-wei Wang2, Xun Xue3 |
| 1 School of Environment, Tsinghua University, Beijing 100084, China;
2 School of Metallurgy and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China;
3 Beijing Shenwu Environment & Energy Technology Co., Ltd., Beijing 102200, China |
|
|
|
|
Abstract Sintering basic characteristics of fourteen iron ores were comprehensively evaluated using micro-sinter and grey relational analysis methods. The results show that magnetite has a low assimilability, high bonding phase strength, and high crystal strength. Hematite presents a good assimilability, while limonite exhibits a strong assimilability, but the bonding phase strength and crystal strength of these two kinds of iron ores are comparatively low. Great difference in liquid flowability exists for the same kind of iron ores. When the assimilation temperature of the sinter mixture is too high, limonite can be added; when the bonding phase strength or crystal strength of the sinter mixture is too low, magnetite can be added. The liquid fluidity of the sinter mixture can be adjusted according to the ratios of corresponding iron ores. Grey relational analysis is an effective method to evaluate the comprehensive sintering characteristics of iron ores, which can provide theoretical basis for the purchasing department of the steel enterprises.
|
|
Received: 24 March 2018
Published: 04 December 2018
|
|
|
|
| Cite this article: |
|
Dong-hui Liu,Jun-hua Li,Yue Peng, et al. Comprehensive evaluation of sintering basic characteristics of iron ore based on grey relational analysis[J]. Journal of Iron and Steel Research International, 2019, 26(7): 691-696.
|
|
|
|
| [1] |
Xiao-hui Fan, Yan-nan Wang, Min Gan, Zhi-yun Ji, Yang Zhou, Xu-ling Chen. Thermodynamic analysis and reaction behaviors of alkali metal elements during iron ore sintering[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(6): 558-566. |
| [2] |
Lei Guo, Jin-tao Gao, Sheng-ping Zhong, Zhan-cheng Guo. Phosphorus migration mechanism between iron and high phosphorus gangue phase at high temperatures[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(2): 113-122. |
| [3] |
Lei Guo, Jin-tao Gao, Sheng-ping Zhong, Qi-peng Bao, Zhan-cheng Guo. In situ observation of iron ore particle reduction above 1373 K by confocal microscopy[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(1): 32-41. |
| [4] |
Yuan-dong Pei,, . Sheng-li Wu . Xiao-jing Shao, . Zhi-xing Zhao, . Gang An . Ze-jun Ma, . Wei-dong Zhang,. Establishment and industrial practice of high-temperature process evaluation system in sintering[J]. , 2018, 25(9): 910-922. |
| [5] |
Hong-ming Long, ? Qi Shi ? Hong-liang Zhang ? Ru-fei Wei ? Tie-jun Chun ? Jia-xin Li. Application status and comparison of dioxin removal technologies for iron ore sintering process[J]. , 2018, 25(4): 357-365. |
| [6] |
Ya-ting Tang . Man-sheng Chu . Jue Tang . Li-hua Gao . Zheng-gen Liu. Oxidation mechanism and non-isothermal kinetic studies on carbonate iron ore by thermogravimetric analysis[J]. , 2018, 25(12): 1223-1231. |
|
|
|
|
2019, Vol. 26 