| Effect of compression deformation on precipitation phase behavior of B-containing S31254 super austenitic stainless steel |
| Jin-gang Bai1,2, Yi-shi Cui1, Jian Wang1, Nan Dong1, Muhammad Saqlain Qurashi1, Hai-rui Wei2, Yong-chao Yang2, Pei-de Han1 |
| 1 College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024, Shanxi, China; 2 State Key Laboratory of Advanced Stainless Steel Materials, Taiyuan 030003, Shanxi, China |
|
|
|
|
Abstract Effects of compression deformation on the sigma-phase precipitation behavior of B-containing S31254 stainless steel after solution treatment were studied using the Gleeble compression test. The cold and hot processing characteristics of B-containing S31254 stainless steel were evaluated, and the results show that the speed of compression deformation increased the precipitation rate of the sigma phase, and the location of precipitation extended from the austenite grain boundary to the original hot rolling deformation area. During cold deformation at room temperature, the precipitation rate increased when the deformation reached at 40%. Deformation at 950 °C affected precipitation more obviously. At 1074 °C, when the deformation reached 20%, the precipitated phases started increasing, and above this deformation range, precipitation began decreasing. Also, at 1074 °C, the deformation accelerated the precipitation of sigma phase; but with deformation, there was a change in critical temperature for the sigma-phase excursion. The precipitation position of the sigma phase is strongly related to the area of the original hot rolling deformation. With an increase in the deformation amount, precipitates in this region appeared as coarse-grained, skeletal, and network-like features.
|
|
Received: 02 April 2018
Published: 13 November 2018
|
|
|
|
| Cite this article: |
|
Jin-gang Bai,Yi-shi Cui,Jian Wang, et al. Effect of compression deformation on precipitation phase behavior of B-containing S31254 super austenitic stainless steel[J]. Journal of Iron and Steel Research International, 2019, 26(7): 712-719.
|
|
|
|
| [1] |
Chen Dong, Hui-bin Wu, Xi-tao Wang. Effect of cooling rate on microstructure, hardness, and residual stress of 0.28C–0.22Ti wear-resistant steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(8): 866-874. |
| [2] |
Chao-lei Zhang, Wen Fang, Bao-run Cai, Xiao-hang Sun, Ya-zheng Liu. Austenite grain growth and its effect on splitting fracture property of a V–N microalloyed medium carbon steel connecting rod[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(8): 875-881. |
| [3] |
Hua Zhang, Yan-xin Wu, Qiu-ju Li, Xin Hong. Effect of matrix structure on mechanical properties and dry rolling– sliding wear performance of alloyed ductile iron[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(8): 888-897. |
| [4] |
Xin-ping Xiao, Gen-hao Shi, Shu-ming Zhang, Yu-wei Gao, Qing-feng Wang, Fu-cheng Zhang. Effect of increased nitrogen content on continuous cooling transition of γ→α in hot-deformed low-C Mo–V–Ti steels[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(7): 733-742. |
| [5] |
Hong-bin Li, Xiao-ping Zheng, De-cheng Wan, Lian-sheng Chen. Effect of time interval on microstructure evolution of medium carbon steel during warm deformation[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(6): 602-610. |
| [6] |
Hou-long Liu, Ming-yu Ma, Ling-ling Liu, Liang-liang Wei, Li-qing Chen. Effect of W addition on hot deformation and precipitation behaviors of 19Cr2Mo ferritic stainless steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(5): 425-434. |
|
|
|
|
2019, Vol. 26 