Effect of Al2O3/TiO2/Na2O on enrichment of phosphorus in P-bearing steelmaking slag |
Kan Yu 1 , Yan-ling Zhang 1 , Feng-shan Li 1 , Ming Gao 1 |
1 State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China |
|
|
Abstract To explore the influence of Al 2 O 3 /TiO 2 /Na 2 O on the mineralogical structure and phosphorus enrichment of converter slag, phosphorus enrichment and distribution in the CaO–SiO 2 –Fe 2 O 3 –MgO–Al 2 O 3 /TiO 2 /Na 2 O slag system were experimentally examined. The results show that phosphorus mainly exists in an n2CaO SiO 2 –3CaO P 2 O 5 (nC 2 S–C 3 P) solid solution. Al 2 O 3 /TiO 2 /Na 2 O is beneficial for phosphorus enrichment in the CaO–SiO 2 –Fe 2 O 3 –MgO slag system to various degrees. This allows screening and separation of the enriched phase in the slag. When Al 2 O 3 content was increased from 0 to 15%, the P 2 O 5 content in the P-rich phase increased from 13.88 to 21.32%, and the area of the P-rich phase decreased from 57.50 to 37.87%. When the TiO 2 content was increased from 0 to 10%, the content of P2O5 in the P-rich phase increased from 13.88 to 22.90%, and the area of the P-rich phase decreased from 57.50 to 39.20%. When the contents of Al 2 O 3 and TiO 2 were increased, the previously formed nC 2 S–C 3 P solid solution transformed into n0C 2 S–C 3 P (n\ n0) with higher phosphorus content. Na 2 O had no significant effect on phosphorus enrichment, but exerted significant influence on the area of the P-rich phase. When the Na 2 O content was increased from 0 to 8%, the previously formed nC 2 S–C 3 P solid solution gradually became Na 2 Ca 4 (PO 4 ) 2 SiO 4 , and the area of the P-rich phase increased from 57.50 to 68.50%. With increasing the content of ATN (a mixture with a mass ratio of Al 2 O 3/TiO 2 /Na 2 O = 15:4:3) from 0 to 30%, the content of P 2 O 5 increased from 13.88 to 42.10% and the area of the P-rich phase decreased from 54.92 to 18.40%.
|
|
|
|
|
Cite this article: |
Kan Yu,Yan-ling Zhang,Feng-shan Li, et al. Effect of Al2O3/TiO2/Na2O on enrichment of phosphorus in P-bearing steelmaking slag[J]. Journal of Iron and Steel Research International, 2019, 26(8): 796-805.
|
|
|
|
[1] |
Jun-xiang Guo, Ling-ling Zhang, Wen-bin Dai, Li-ying Qi, Ru-fei Wei, Da-qiang Cang. Mechanisms of ultrafine particle formation during coal combustion in a new swirl modification device[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(1): 11-19. |
[2] |
Ping Shen Qian-kun Yang Dong Zhang Yan-xin Wu, Jian-xun Fu. Application of tellurium in free-cutting steels[J]. , 2018, 25(8): 787-795. |
[3] |
Sunday Abraham . Rick Bodnar . Justin Raines . Yufeng Wang. Inclusion engineering and metallurgy of calcium treatment[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2018, 25(2): 133-145. |
[4] |
Pei-sheng Liu*,Guang Cui,Yi-jiao Guo,Jing-he Chen,Zi-xuan Yang. A novel sort of porous ceramic foam ball with modified surface for arsenic removal from aqueous solution[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 661-667. |
[5] |
Cheng-song Liu,Xiao-qin Liu,*,Hong-wei Ni,Shu-feng Yang,Jing-she Li,Fei Ye. Effect of vanadium on modification of inclusions in Mn- and Si-deoxidized steel during heat treatment at 1473 K[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 520-528. |
[6] |
Yong-jiang Huang,,,*,Peng Xue,Xiang Cheng,Ya-ming Wang,Fu-yang Cao,**, Zhi-liang Ning, Jian-fei Sun,. Plasticity improvement of a Zr-based bulk metallic glass by micro-arc oxidation[J]. Chinese Journal of Iron and Steel, 2017, 24(4): 416-420. |
|
|
|
|