| Effect of cooling rate on microstructure and inclusion in non-quenched and tempered steel during horizontal directional solidification |
| Hui Liu1, Zong-ze Huang2, Da-jiang Yu2, De-lin Hu1, Hong-gang Zhong1, Qi-jie Zhai1, Jian-xun Fu1 |
| 1 State Key Laboratory of Advanced Special Steel, School of Materials Science and Engineering, Shanghai University, Shanghai 200072, China 2 State Key Laboratory of Development and Application Technology of Automotive Steels (Baosteel Group), Shanghai 201900, China |
|
|
|
|
Abstract In order to investigate the relationship between microstructure and MnS inclusion in non-quenched and tempered steel, and cooling rate during horizontal directional solidification, 49MnVS steel was used to conduct the experiments with a selfdesigned device. The mathematical effect of cooling rate on dendritic arm spacing and mean diameter of MnS particles (dMnS) were determined by using linear regression method. The results show that the length of dendrite from solid–liquid interface to end-solidification decreased with increasing the withdrawal velocity (#). dMnS has a similar value in the area of the steady directional solidification; the value of dMnS was 4.1, 3.6, 3.3, 2.8 and 2.3 lm at withdrawal velocity of 50, 75, 100, 150 and 200 lm/s, respectively. dMnS increased with reducing # or RC (interface cooling rate). MnS precipitated in the gaps between dendrites and was influenced by secondary dendritic arm spacing. Besides, a new concept of the ‘Precipitation Unit Space’ (PUS) was proposed and the relationships between dMnS, VPUS (volume of PUS) and RC were obtained.
|
|
|
|
|
|
| Cite this article: |
|
Hui Liu,Zong-ze Huang,Da-jiang Yu, et al. Effect of cooling rate on microstructure and inclusion in non-quenched and tempered steel during horizontal directional solidification[J]. Journal of Iron and Steel Research International, 2019, 26(9): 973-982.
|
|
|
|
| [1] |
Xin-gang Liu, Can Wang, Qing-feng Deng, Bao-feng Guo. High-temperature fracture behavior of MnS inclusions based on GTN model[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(9): 941-952. |
| [2] |
Hao-jian Duan, Ying Zhang, Ying Ren, Li-feng Zhang. Distribution of TiN inclusions in Ti-stabilized ultra-pure ferrite stainless steel slab[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(9): 962-972. |
| [3] |
Chen Dong, Hui-bin Wu, Xi-tao Wang. Effect of cooling rate on microstructure, hardness, and residual stress of 0.28C–0.22Ti wear-resistant steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(8): 866-874. |
| [4] |
Ting DAN. Analysis on Cracking Failure in Typical Cases of Folding Defect Based on Fastener [J]. , 2019, 37(4): 0-0. |
| [5] |
Shang-lin Lv . Zhong-min Yang . Bin Zhang, . Jie Chen . Ying Chen . Xiao-bin Li. Corrosion passive behaviour duplexstainlesssteelat different rates simulated marine-environmentsolution[J]. , 2018, 25(9): 943-953. |
| [6] |
Ping Shen Qian-kun Yang Dong Zhang Yan-xin Wu, Jian-xun Fu. Application of tellurium in free-cutting steels[J]. , 2018, 25(8): 787-795. |
|
|
|
|
2019, Vol. 26 