| Interface reaction of high-strength low-alloy steel with Al–43.4Zn–1.6Si (wt.%) metallic coating |
| Wang-jun Peng1,2,3, Guang-xin Wu1,2,3, Yi Cheng1,2,3, Jie-yu Zhang1,2,3 |
1 State Key Laboratory of Advanced Special Steel, Shanghai University, Shanghai 200072, China
2 Shanghai Key Laboratory of Advanced Ferrometallurgy, Shanghai University, Shanghai 200072, China
3 School of Materials Science and Engineering, Shanghai University, Shanghai 200072, China |
|
|
|
|
Abstract The microstructure, elemental distribution, phase composition, and thickness of intermetallic layers between high-strength low-alloy steel (H420)/mild carbon steel (DC51) and Al–43.4Zn–1.6Si (wt.%) (galvalume, GL) alloy were comparatively investigated. The experimental results reveal that the interfacial reaction layer was composed of Fe2Al5, Fe4Al13, and Al8Fe2Si intermetallic compounds. Moreover, the growth curves of the Fe2Al5 and Fe4Al13 intermetallic layers fit the parabolic law well, and the total thickness of the intermetallic layers of H420 + GL was almost the same as that of DC51 + GL. However, the thickness of the Fe2Al5 layer in H420 + GL was thinner than that in DC51 + GL. In addition, first-principle calculations were performed to explore the effect of Mn on the growth of the Fe2Al5 intermetallic phase, and the results indicate that Mn substitution in Fe2Al5 removes electronic charge from the Al atoms, thus decreasing the thickness of the Fe2Al5 interface layer.
|
|
Received: 01 June 2018
Published: 25 December 2019
|
|
|
|
| Cite this article: |
|
Wang-jun Peng,Guang-xin Wu,Yi Cheng, et al. Interface reaction of high-strength low-alloy steel with Al–43.4Zn–1.6Si (wt.%) metallic coating[J]. Journal of Iron and Steel Research International, 2019, 26(12): 1304-1314.
|
|
|
|
| [1] |
Jin-wei Lei, Kai-ming Wu, Yu Li, Ting-ping Hou, Xing Xie, R.D.K. Misra. Effects of Zr addition on microstructure and toughness of simulated CGHAZ in high-strength low-alloy steels[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(10): 1117-1125. |
| [2] |
Ebrahim Mortazavi,Reza Amini Najafabadi,Amirhossein Meysami*. Effect of heat input on microstructure and mechanical properties of dissimilar joints of AISI 316L steel and API X70 high-strength low-alloy steel[J]. , 2017, 24(12): 1248-1253. |
| [3] |
Gu-jun CHEN,Sheng-ping HE,Yin-tao GUO,Bo-yi SHEN,Shuo ZHAO,Qian WANG. Optimization of Calcium Addition to High-strength Low-alloy Steels[J]. Chinese Journal of Iron and Steel, 2015, 22(7): 590-597. |
|
|
|
|
2019, Vol. 26 