Effects of solution treatment and cold rolling on structure and tensile properties of hot-rolled Ti–7.5Mo alloy |
Yen-chun Chen1, Chien-ping Ju1, Jiin-huey Chern Lin1 |
1 Department of Materials Science and Engineering, ChengKung University, Taiwan 70101, China |
|
|
Abstract The effects of solution treatment (ST) and cold rolling (CR) on structure and tensile properties of a heavily hot-rolled (HR) Ti–7.5Mo alloy were investigated. Experimental results indicated that, after HR with a one-pass 65% reduction in thickness, the pores in as-received samples substantially disappeared, the misorientation angle distribution became broader, and grain texture shifted toward <10-10>. Post-HR ST produced an orthorhombic α''-phase with fine needle-type morphology and caused misorientation to narrow down to 55°–65° with substantially random texture; post-ST CR caused misorientation shift toward high-angle side and texture toward <10-10> and <2-1-10>. With an increase in reduction in thickness, α' (102) intensity increased at the expense of two adjacent (112)/(022) α''-peaks. All X-ray diffraction, metallography and electron backscattered diffraction on scanning electron microscope results indicated that pre-ST HR did not affect the formation of the desired low-modulus α''-phase when the alloy was subsequently solution-treated. From a practical point of view, the most optimal tensile properties may be found in the sample solution-treated at 900 °C for 30 min and cold-rolled by a 20% reduction in thickness, which demonstrated a yield strength of 924 MPa, an ultimate tensile strength of 933 MPa, a tensile modulus of 73 GPa, and an elongation of 26%.
|
Received: 15 November 2018
Published: 25 December 2019
|
|
|
|
Cite this article: |
Yen-chun Chen,Chien-ping Ju,Jiin-huey Chern Lin. Effects of solution treatment and cold rolling on structure and tensile properties of hot-rolled Ti–7.5Mo alloy[J]. Journal of Iron and Steel Research International, 2019, 26(12): 1366-1375.
|
|
|
|
[1] |
Yang Cao, Chong Luo, Lin Zhao, Yun Peng, Liang Song, Cheng-yong Ma, Zhi-ling Tian, Min-lin Zhong, Yan-jie Wang. Microstructural evolution and mechanical properties of laser-welded joints of medium manganese steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(1): 75-87. |
[2] |
Xian-hong Han, Cheng-long Wang, Yuan-yuan Li, Gang Liu. Effects of quenching and partitioning process on mechanical properties of TRIP780 steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(9): 991-999. |
[3] |
Wei-jun Hui, Zhan-hua Wang, Zhi-bao Xu, Yong-jian Zhang, Xiao-li Zhao. Hydrogen embrittlement of a microalloyed bainitic forging steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(9): 1011-1021. |
[4] |
Hai-long Yi, Lu-ran Zhang, Rui-hai Duan, Xin-zeng Liang. Microstructure–mechanical property relationship in Ti–Mo microalloyed steel with random and interphase precipitates[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(8): 838-845. |
[5] |
Jun-yu Tian, Guang Xu, Ming-xing Zhou, Hai-jiang Hu, Zheng-liang Xue. Effects of Al addition on bainite transformation and properties of high-strength carbide-free bainitic steels[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(8): 846-855. |
[6] |
Chen Dong, Hui-bin Wu, Xi-tao Wang. Effect of cooling rate on microstructure, hardness, and residual stress of 0.28C–0.22Ti wear-resistant steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(8): 866-874. |
|
|
|
|