Influence of reaction of Al2O3 and carbonaceous materials in Al2O3–C refractories on aluminum and carbon pick-up of iron |
Yao-wu Wei1, Yan-jun Dong1, Tao Zhang1, Jun-feng Chen1, Wen Yan1 |
1 The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081, Hubei, China |
|
|
Abstract Carbon-containing Al2O3 refractory crucibles and pure Al2O3 refractory crucible were fabricated to study the effect of carbon-containing Al2O3–C refractories on aluminum and carbon pick-up of iron. Refractory crucibles with pure iron powder were placed in a vacuum induction furnace and heated at 1600 °C for regular time under flowing argon atmosphere. The Al and C contents of iron samples were analyzed, and iron samples were also investigated using a field scanning electron microscope equipped with energy-dispersive spectroscope. The results showed that carbon materials did affect the interaction of (Al2O3–C)/Fe system, carbothermal reduction in alumina occurred in the reaction system and the extent of reactions depended on the kinds of carbon materials.
|
Received: 28 August 2018
Published: 25 January 2020
|
|
|
|
Cite this article: |
Yao-wu Wei,Yan-jun Dong,Tao Zhang, et al. Influence of reaction of Al2O3 and carbonaceous materials in Al2O3–C refractories on aluminum and carbon pick-up of iron[J]. Journal of Iron and Steel Research International, 2020, 27(1): 55-61.
|
|
|
|
[1] |
Ya-yu LI,Zhen-nan LIU,Dong-ping TAO. An Estimation of Component Activity of Vanadium-bearing Liquid Iron and Transition Temperature of Vanadium Oxidization Using MIVM[J]. Chinese Journal of Iron and Steel, 2015, 22(7): 557-565. |
[2] |
Ran LIU,,Xin-yuan ZHANG,,Xing-juan WANG,,Ya-na QIE,,Qing L,,Fu GAO,. Preparation and Oxidation Resistance of BN-MgAlON Composites by Hot-pressing Sintering[J]. Chinese Journal of Iron and Steel, 2015, 22(5): 423-430. |
[3] |
Tong-sheng ZHANG,De-yong WANG,Mao-fa JIANG. Effect of Magnesium on Evolution of Oxide and Sulphide in Liquid Iron at 1873 K[J]. Chinese Journal of Iron and Steel, 2014, 21(12): 1073-1080. |
|
|
|
|