| Orientation gradient on surface of non-oriented electrical steel annealed by γ → α transformation |
| Jin-hua Wang1, Ping Yang1, Wei-min Mao1, Feng-e Cui1 |
| 1 School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China |
|
|
|
|
Abstract The microstructures and textures of the non-oriented electrical steel sheets under various annealing conditions were investigated. The orientation gradient in the interior of grains appeared on the surface of steel sheets after α → γ → α transformation in various atmospheres. The orientation gradient that appeared on the surface was inherited into the center of the steel sheet in H2 atmosphere, while that appeared only in the grains of the surface layer during γ → α transformation with N2 atmosphere. The thin oxide scale was generated in various atmospheres containing traces of O2 and H2O. The formation mechanism of orientation gradient is related to the thermal stress caused by the difference of thermal expansion coef?cients between the oxide scale and the thin ferrite on the surface. The combined effect of phase transformation stress and thermal stress caused the plastic deformation of the thin ferrite grains on the surface in the initial stage of γ → α transformation, and then the orientations of the thin ferrite grains gradually rotated and caused the orientation gradient in the interior of grains.
|
|
Received: 04 October 2018
Published: 25 January 2020
|
|
|
|
| Cite this article: |
|
Jin-hua Wang,Ping Yang,Wei-min Mao, et al. Orientation gradient on surface of non-oriented electrical steel annealed by γ → α transformation[J]. Journal of Iron and Steel Research International, 2020, 27(1): 88-95.
|
|
|
|
| [1] |
Xiao‑long Liang, Hui Wang, Qian‑fu Pan, Ji‑yun Zheng, Hui‑qun Liu, Rui‑qian Zhang, Yang Xu, Yu Xu, Dan‑qing Yi. Recrystallization and mechanical properties of cold-rolled FeCrAl alloy during annealing[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(5): 549-565. |
| [2] |
Xiao-dong Li, Jin Liu, Yan-yan Zhu, Xu Cheng, Dong Liu, Ji-kui Zhang. Solid-state phase transformation of TC11 titanium during unstable thermal cycling in laser melting deposition process[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(7): 743-750. |
| [3] |
Wen-tao Wang, Jiao Zhang, Feng-li Sui, Zhi-xia Zhang, Hong-yun Bi. A comparison of deformation, microstructure, mechanical properties and formability of SUS436L stainless steel in tandem and reversible cold rolling processes[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(5): 442-451. |
| [4] |
Zhi-yuan Chen, Ying-xia Qu, Christiaan Zeilstra, Jan Van Der Stel, Jilt Sietsma, Yong-xiang Yang. Prediction of density and volume variation of hematite ore particles during in-flight melting and reduction[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(12): 1285-1294. |
| [5] |
Hendrik Hotz, Benjamin Kirsch, Steven Becker, Ralf Mu¨ ller, Jan C. Aurich. Combination of cold drawing and cryogenic turning for modifying surface morphology of metastable austenitic AISI 347 steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(11): 1188-1198. |
| [6] |
Si-lian Chen, Zhao-xi Cao, Chang Wang, Chong-xiang Huang, Dirk Ponge, Wen-quan Cao. Effect of volume fraction and mechanical stability of austenite on ductility of medium Mn steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(11): 1209-1218. |
|
|
|
|
2020, Vol. 27 