Effect of final electromagnetic stirring on solidification microstructure of GCr15 bearing steel in simulated continuous casting |
Dan-qing Jiang1,2, Rui Wang1,2, Qiong Zhang1,2, Zhen-qiang Zhang1,2, Ting-sheng Tu1,2, Jiang Wang1,2, Zhong-ming Ren1,2 |
1 School of Materials Science and Engineering, Shanghai University, Shanghai 200444, China; 2 State Key Laboratory of Advanced Special Steel, Shanghai University, Shanghai 200444, China |
|
|
Abstract The effect of final electromagnetic stirring on the solidification structure, element segregation, and carbides of GCr15 bearing steel was investigated. The experiment of continuous casting of the steel was carried out by using a continuous casting physical simulation apparatus with the final electromagnetic stirring. The liquid core profile was revealed by the pour-out method during the solidification process. Eight ingots were produced under different electromagnetic stirring parameters for comparison. The results show that, at the final stage of solidification, intense electromagnetic stirring exacerbates the central carbon segregation, resulting in more serious precipitation of the primary carbides. It is also found that the carbides in the segregation area are dominantly M3C type, together with a small amount of M7C3-type and M3C2- type carbides. In this physical simulation model, the optimal stirring parameters to obtain a fine and homogeneous structure are the liquid pool width of 15 mm, current intensity of 150 A, and stirring frequency of 5 Hz.
|
|
|
|
|
Cite this article: |
Dan-qing Jiang,Rui Wang,Qiong Zhang, et al. Effect of final electromagnetic stirring on solidification microstructure of GCr15 bearing steel in simulated continuous casting[J]. Journal of Iron and Steel Research International, 2020, 27(2): 141-147.
|
|
|
|
[1] |
Ran Niu, Bao-kuan Li, Zhong-qiu Liu, Xiang-long Li. Effect of strip feeding into mold on fluid flow and heat transfer in continuous casting process[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(3): 295-309. |
[2] |
Zhi-ming Li, Xiang Li, Lei Yang, Zheng-yan Shen, Bi-lei Wang, Shun-li Zhao, Gao-fei Liang, Chang-jiang Song. Effect of coiling and annealing temperatures on yield point behavior of low?carbon steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(3): 325-333. |
[3] |
Zhong-kuai Jiang, Zhi-jian Su, Cheng-qian Xu, Jin Chen, Ji-cheng He. Abnormal mold level fluctuation during slab casting of peritectic steels[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(2): 160-168. |
[4] |
Ding-li Zheng, Cheng-bin Shi, Zhi-jun Li, Jing Li, Jung-wook Cho. Effect of SiO2 substitution with Al2O3 during high-Al TRIP steel casting on crystallization and structure of low-basicity CaO–SiO2-based mold flux[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(1): 33-41. |
[5] |
Hai-biao Lu, Chang-gui Cheng, Yang Li, Xu-feng Qin, Yan Jin. Flow and heat transfer of liquid slag in a continuous casting mold[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(9): 926-940. |
[6] |
Yan-mo Li, Yong-chang Liu, Li-ming Yu, Chen-xi Liu, Chong Li, Yuan Huang, Hui-jun Li, Zong-qing Ma. Effect of deformation twinning on high-temperature performance of cold-rolled S31042 steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(7): 704-711. |
|
|
|
|