| Reaction kinetics during direct alloying of manganese ore cored wire |
| Wei Wu1, Qi Gao1, Bo Zhang1, Hua-dong Meng1, Lu Lin1,2, Jia-qing Zeng |
| 1Metallurgical Technology Research Department, Central Iron and Steel Research Institute, Beijing 100081, China; 2 State Key Laboratory of Refractory and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081, Hubei, China |
|
|
|
|
Abstract In order to increase the reaction rates between the molten steel and the slag and cut down the reduction time when the top slag of manganese ore is added into the molten steel, a method of directly alloying manganese ore has been experimented in a 500-kg induction furnace. The results show that the manganese yield is greater than 90% when the wire feeding method is used. The manganese yield is 43.26% within 1 min. In contrast, the manganese yield for the top-slag adding process is only 10.98% for the same duration. The mass transfer rate of the manganese is greater in the molten steel than in the slag, and the limiting factor is the mass transfer rate of the manganese in the slag in the period of 10?30 min. The slag composition area is closer to the area of high melting point for the wire feeding method than for the top-slag adding process. During the slagging process, refining slag composed of CaO and SiO2 is formed after 15 min; after 25?30 min, refining slag with a high basicity is formed and consists of CaO, SiO2 and Al2O3.
|
|
|
|
|
|
| Cite this article: |
|
Wei Wu,Qi Gao,Bo Zhang, et al. Reaction kinetics during direct alloying of manganese ore cored wire[J]. Journal of Iron and Steel Research International, 2020, 27(3): 282-294.
|
|
|
|
| [1] |
Romie D. Laranjo Nathaniel M. Anacleto. Direct smelting process for stainless steel crude alloy recovery from mixed low-grade chromite, nickel laterite and manganese ores[J]. , 2018, 25(5): 515-523. |
| [2] |
Jian Gou. Zheng-jun Liu . Hua Jia. Effects of Nb on microstructure and wear resistance of Fe–Cr–C–B surfacing alloy[J]. , 2018, 25(2): 243-251. |
| [3] |
Hai-yun LIU,Zhi-liang SONG,Qing CAO,Shao-ping CHEN,Qing-sen MENG. Microstructure and Properties of Fe-Cr-C Hardfacing Alloys Reinforced with TiC-NbC[J]. Chinese Journal of Iron and Steel, 2016, 23(3): 276-280. |
| [4] |
YANG Ke,ZHANG Zhi-xi,HU Wang-qin,BAO Ye-feng,JIANG Yong-feng. A New Type of Submerged-Arc Flux-Cored Wire Used for Hardfacing Continuous Casting Rolls[J]. Chinese Journal of Iron and Steel, 2011, 18(11): 74-79. |
|
|
|
|
2020, Vol. 27 