A novel laminated metal composite with superior interfacial bonding composed of ultrahigh strength maraging steel and 316L stainless steel |
Le Zhang1,2, Wei Wang1,3, M. Babar Shahzad1, Yi yin Shan1,3, Ke Yang1 |
1 Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, Liaoning, China; 2 School of Materials Science and Engineering, University of Science and Technology of China, Hefei 230026, Anhui, China; 3 Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, Liaoning, China |
|
|
Abstract A 5-layer laminated metal composite composed of ultrahigh-strength maraging steel and ductile 316L stainless steel was fabricated by hot pressing in vacuum and post-heat treatment. Microstructure characterization on hierarchical structure of the composite before and after heat treatment was made by optical microscopy, scanning electron microscopy and electron back-scattered diffraction technique, respectively. Meanwhile, the difference of mechanical performance on both sides of the interface was characterized by nano-hardness testing. Uniaxial tensile test showed that superior interfacial bonding was achieved due to the micro-‘bite’ structure between the two steels without obvious defects or oxides at the interface and with coordinated deformation of the two components. Thus, a laminated metal composite consisting of two different constituents with extreme difference in strength can be well fabricated.
|
|
|
|
|
Cite this article: |
Le Zhang,Wei Wang,M. Babar Shahzad, et al. A novel laminated metal composite with superior interfacial bonding composed of ultrahigh strength maraging steel and 316L stainless steel[J]. Journal of Iron and Steel Research International, 2020, 27(4): 433-439.
|
|
|
|
[1] |
Rui-qi Yao, Xing-you Lang, Qing Jiang. Recent advances of nanoporous metal-based catalyst: synthesis, application and perspectives[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(8): 779-795. |
[2] |
Wen-shu Zhang, Cai-li Zhang, Nan Dong, Jian-guo Li, Pei-de Han, Zhu-xia Zhang, Li-xia Ling. Surface adsorption and diffusion of N on c-Fe–Al (111) using first principles calculations[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(8): 882-887. |
[3] |
Jin-gang Bai, Yi-shi Cui, Jian Wang, Nan Dong, Muhammad Saqlain Qurashi, Hai-rui Wei, Yong-chao Yang, Pei-de Han. Effect of compression deformation on precipitation phase behavior of B-containing S31254 super austenitic stainless steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(7): 712-719. |
[4] |
Wan-lin Wang, Er-zhuo Gao, Le-jun Zhou, Lei Zhang, Huan Li. Effect of Al2O3/SiO2 and CaO/Al2O3 ratios on wettability and structure of CaO–SiO2–Al2O3-based mold flux system[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(4): 355-364. |
[5] |
Yan-sen Hao, Jian Li, Wan-chun Liu, Wei-na Zhang, Zhen-yu Liu. On microstructure characterization of Fe–Cr–Ni–Mo–N super-austenitic stainless steel during hot deformation[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(10): 1080-1087. |
[6] |
Xi-yang Chai, . Tao Pan . Feng Chai . Xiao-bing Luo . Hang Su . Zhi-gang Yang . Cai-fu Yang. Interlayer engineering for titanium clad steel by hot roll bonding[J]. , 2018, 25(7): 739-745. |
|
|
|
|