| Effects of metallic microstructures on fatigue fracture of Q345 steel |
1 School of Aeronautics and Astronautics, Sichuan University, Chengdu 610065, Sichuan, China
2 Failure Mechanics and Engineering Disaster Prevention and Mitigation Key Laboratory of Sichuan Province, Sichuan University, Chengdu 610065, Sichuan, China
3 Department of Mechanical Engineering, Kyushu University, Fukuoka 819-0395, Japan
4 School of Materials Science and Engineering, Jiangxi University of Science and Technology, Ganzhou 341000, Jiangxi, China |
|
|
|
|
Abstract Effects of high-frequency cyclic loading on the banded ferrite–pearlite steel were analyzed through crack initiation and propagation. Interfaces of ferrite and pearlite colony with a small angle deviation from the loading axis were verified to be the most potential sites to fabricate the microcracks caused by the high strain gradient. The initial crack extension inside ferrite grain was driven by shear stress in model II along the direction with a 45° angle to the loading axis. Banded pearlite colony and the high-angle grain boundaries were considered as the dominant factors that promote the fatigue resistance of the material through arousing crack deflection in short crack propagation range and crack branching in long crack propagation range to reduce the crack propagation driving force in the crack tip. P–S–N curves were used to quantify the dispersion of fatigue lifetimes and evaluate the effect of elevated volume content of pearlite colony on the fatigue performance of the material.
|
|
Received: 01 May 2019
Published: 25 June 2020
|
|
|
|
| Cite this article: |
|
Hanqing Liu. Effects of metallic microstructures on fatigue fracture of Q345 steel[J]. Journal of Iron and Steel Research International, 2020, 27(6): 702-709.
|
|
|
|
| [1] |
Hu Chen, Chi Zhang, Hao Chen, Zhi-gang Yang, Lei Chen. Understanding microstructure-evolution-dependent fracture behaviors in pearlitic steels[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(3): 334-341. |
| [2] |
Xin-gang Liu, Can Wang, Qing-feng Deng, Bao-feng Guo. High-temperature fracture behavior of MnS inclusions based on GTN model[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(9): 941-952. |
| [3] |
Cao .Chen · Xiao-yong .Zhang,,, · Xiao-jun . Yan ,,, · Jun Ren · Da-wei .Huang · Ming-jing .Qi. Effect of.laser shock peening on.combined low- and.high-cycle fatigue life of.casting and.forging turbine blades[J]. , 2018, 25(1): 108-119. |
| [4] |
Hang-wei Zhou,,Hui-qun Liu,,Dan-qing Yi,,Yu Xiao,,Xiao-long Zhao,Jian Wang,Qi Gao. Effect of α phase on fatigue crack growth of Ti-6242 alloy[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 811-822. |
| [5] |
Li-dong WANG, Feng-lei LIU, Qing-yun ZHAO, Hui-bin WU. CO2 Corrosion and Grooving Corrosion Behavior of the ERW Joint of the Q125 Grade Tube Steel[J]. Chinese Journal of Iron and Steel, 2015, 22(10): 943-948. |
| [6] |
CHENG Hao,LIU Dong,TANG Hai-bo,ZHANG Shu-quan,RAN Xian-zhe,WANG Hua-ming. Effect of Hot Isostatic Pressing on Fatigue Properties of Laser Melting Deposited AerMet100 Steel[J]. Chinese Journal of Iron and Steel, 2013, 20(11): 79-84. |
|
|
|
|
2020, Vol. 27 