Microstructure and properties of hybrid additive manufacturing 316L component by directed energy deposition and laser remelting |
Xiao‑hui Chen1,2, Bo Chen1, Xu Cheng1, Guo‑chao Li1, Zheng Huang1 |
1 National Engineering Laboratory of Additive Manufacturing for Large Metallic, Components and Engineering Research Center, Ministry of Education on Laser Direct Manufacturing for Large Metallic Components, School of Materials Science and Engineering, Beihang University, Beijing 100191, China; 2 Research Center for Processing, AECC Shanghai Commercial Aircraft Engine Manufacturing Co., Ltd., Shanghai 201306, China |
|
|
Abstract Arc additive manufacturing is a high-productivity and low-cost technology for directly fabricating fully dense metallic components. However, this technology with high deposit rate would cause degradation of dimensional accuracy and surface quality of the metallic component. A novel hybrid additive manufacturing technology by combining the benefit of directed energy deposition and laser remelting is developed. This hybrid technology is successfully utilized to fabricate 316L component with excellent surface quality. Results show that laser remelting can largely increase the amount of δ phases and eliminate σ phases in additive manufacturing 316L component surface due to the rapid cooling. This leads to the formation of remelting layer with higher microhardness and excellent corrosion resistance when compared to the steel made by directed energy deposition only. Increasing laser remelting power can improve surface quality as well as corrosion resistance, but degrade microhardness of remelting layer owing to the decrease in δ phases.
|
|
|
|
|
Cite this article: |
Xiao‑hui Chen,Bo Chen,Xu Cheng, et al. Microstructure and properties of hybrid additive manufacturing 316L component by directed energy deposition and laser remelting[J]. Journal of Iron and Steel Research International, 2020, 27(7): 842-848.
|
|
|
|
[1] |
Jun Zhao, Hai-bin Zuo, Chao Ling, Wen-tao Guo, Jing-song Wang, Qing-guo Xue. Microstructure evolution of coke under CO2 and H2O atmospheres[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(7): 743-754. |
[2] |
Rui‑wu Li, Zheng Zhang, Jian‑wei Li, Ke‑xin Ma, Yuan‑yuan Guo, Yan‑wen Zhou, Fa‑yu Wu. Surface modification of 316L stainless steeldiamond-like carbon films[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(7): 867-874. |
[3] |
Wan‑lin Wang, Guo‑min Ying, Jie Zeng, Hai‑hui Zhang. Effect of electropulsing treatment on solidification behavior of spring steels in a continuous casting mold simulator[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(6): 656-664. |
[4] |
Chun‑xu Wang, Yuan‑hang Gao, Yong Li, Shun Han, Shao‑zun Liu, Peng‑jie Zhang. Effects of solid-solution temperature on microstructure and mechanical properties of a novel 2000 MPa grade ultra-high-strength steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(6): 710-718. |
[5] |
Xiao-ping Ma, Dian-zhong Li. Coalescence-dominated microstructure evolution during solidification of 20SiMn steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(5): 506-516. |
[6] |
Ming Lei, Wei‑jun Hui, Jiao‑jiao Wang, Yong‑jian Zhang, Xiao‑li Zhao. Microstructure and mechanical properties of hot-rolled V-microalloyed Al-containing medium-Mn steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(5): 537-548. |
|
|
|
|