Effect of tempering on the bonding characteristics of cross wedge rolling 42CrMo/Q235 laminated shafts |
Shuai Zhu1, Wen-fei Peng1, Xue-dao Shu1 |
1 Zhejiang Provincial Key Laboratory of Part Rolling Technology, Ningbo University, Ningbo 315211, Zhejiang, China |
|
|
Abstract
To further improve the comprehensive properties of 42CrMo/Q235 laminated shafts produced by cross wedge rolling, the heat treatment of the shafts was studied. Tensile and bending tests were carried out to compare the changes in mechanical properties before and after heat treatment. The results showed that the interfacial bonding strength increased most after tempering at 350 °C for 45 min. The microstructure of the interface was observed using a digital microscope. The results showed that the dispersed oxides on the interface were basically eliminated by using the scheme of tempering at 350 °C and holding for 45 min. The reasons for the change in mechanical properties were explained from the point of the interfacial microstructure. Scanning electron microscopy was used to analyze the micro-morphology of the tensile fracture. It was observed that after tempering at 350 °C and holding for 45 min, the dimple holes became larger and deeper, and the structure of fracture became more uniform and stable. From the point of the tensile fracture morphology, the reasons for the change in mechanical properties were explained as well.
|
Received: 14 September 2019
Published: 25 October 2020
|
|
|
|
Cite this article: |
Shuai Zhu,Wen-fei Peng,Xue-dao Shu. Effect of tempering on the bonding characteristics of cross wedge rolling 42CrMo/Q235 laminated shafts[J]. Journal of Iron and Steel Research International, 2020, 27(10): 1170-1178.
|
|
|
|
[1] |
Ai‑jun Deng, Ding‑dong Fan, Hai‑chuan Wang, Can‑hua Li. Simulation research on oxygen mass transfer between steel and slag in IF steel refning process[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(4): 409-419. |
[2] |
Xin-yang Lü, Zhi-wei Wu, Xiao He, Jun Li, Shao-hong Li, Mao-sheng Yang, Kun-yu Zhao. Effect of deep cryogenic treatment on martensitic lath refinement and nano-twins formation of low carbon bearing steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(1): 105-113. |
[3] |
Wang-jun Peng, Guang-xin Wu, Yi Cheng, Jie-yu Zhang. Interface reaction of high-strength low-alloy steel with Al–43.4Zn–1.6Si (wt.%) metallic coating[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(12): 1304-1314. |
[4] |
Jun Jiang,. Hua Ding . Zong-an Luo . Guang-ming Xie. Interfacial microstructure and mechanical properties of stainless steel clad plate prepared by vacuum hot rolling[J]. , 2018, 25(7): 732-738. |
[5] |
Xiao-rong Yang, Li-feng Ma Guang-ming Liu Guang-hui Zhao Zheng-yi Jiang. Hot-rolling influence of hot rolling on microstructure and mechanical characteristics of explosive-welded FSS/CS laminate[J]. , 2018, 25(5): 572-579. |
[6] |
Ping-hu Chen, · Zhi-lin Liu, · Rui-qing Li, · Chang-jun Qiu · Xiao-qian Li,,. Thermal-sprayed coating of optimally mixed ceramic powders on stainless steel with enhanced corrosion resistance[J]. , 2018, 25(2): 207-212. |
|
|
|
|