Mechanical and tribological properties of graphene nanoplatelets-reinforced titanium composites fabricated by powder metallurgy |
Zhen Cao1,2,3, Jiong-li Li1,2,3, Hai-ping Zhang1,2,3, Wen-bo Li1,2,3, Xu-dong Wang1,2,3 |
1 AECC Beijing Institute of Aeronautical Materials, Beijing 100095, China
2 Beijing Institute of Graphene Technology, Beijing 100094, China
3 Beijing Engineering Research Centre of Graphene Application, Beijing 100095, China |
|
|
Abstract Titanium matrix composite reinforced by graphene nanoplatelets (GNPs) was fabricated via powder metallurgy route. Hot isostatic pressing and hot extrusion were used to consolidate the mixed powder of GNPs and TC4 titanium (Ti) alloy. The microstructures, mechanical properties and sliding wear performance of Ti/GNPs composite had been researched to evaluate the reinforcing effect of GNPs on titanium matrix. Microstructure observation indicates that GNPs could restrain grain growth slightly in titanium matrix. Titanium matrix and graphene exhibit a clean and firm interface formed by means of metallurgical bonding on atomic scale. Compared with the monolithic titanium alloy, the composite with 1.2 vol.% GNPs exhibits significantly improved elastic modulus and strength. The sliding wear test shows that there is an obvious enhancement in the tribological performance of Ti/GNPs composite with 1.2 vol.% GNPs. The results of this work indicate that GNP is an efficient reinforcement material in titanium matrix. The strengthening mechanism including precipitates strengthening, load transfer and grain refinement mechanism of GNPs in titanium matrix was discussed. A modified shear-lag model was used to analyze the reinforcement contribution of the stress transfer mechanism. The calculation shows that the stress load mechanism constitutes the main strengthening mechanism in Ti/GNPs composite.
|
Received: 05 September 2019
Published: 25 November 2020
|
|
|
|
Cite this article: |
Zhen Cao,Jiong-li Li,Hai-ping Zhang, et al. Mechanical and tribological properties of graphene nanoplatelets-reinforced titanium composites fabricated by powder metallurgy[J]. Journal of Iron and Steel Research International, 2020, 27(11): 1357-1362.
|
|
|
|
[1] |
Huang Xie, Yun‑xue Jin, Mu‑ye Niu, Ji‑heng Wang. Effect of multilayer graphene/nano-Fe2O3 composite additions on dry sliding wear behavior of titanium matrix composites[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(9): 1117-1126. |
[2] |
Dan-yang Lin,Nan-nan Zhang,*,Bin He,Guang-wei Zhang,,Yue Zhang,De-yuan Li. Tribological properties of FeCoCrNiAlBx high-entropy alloys coating prepared by laser cladding[J]. Chinese Journal of Iron and Steel, 2017, 24(2): 184-189. |
[3] |
Li-ming TAN,,Yi-wen ZHANG,,Jian JIA,,Shou-bo HAN,. Precipitation of μ Phase in Nickel-based Powder Metallurgy Superalloy FGH97[J]. Chinese Journal of Iron and Steel, 2016, 23(8): 851-856. |
[4] |
Ying KAN,,Shi-hong ZHANG,Li-wen ZHANG,Ming CHENG,Hong-wu SONG,Hong-wei LU. Healing Behavior of Micropores in Powder Metallurgy 316L Stainless Steel during Hot Forging and Heat Treatment[J]. Chinese Journal of Iron and Steel, 2014, 21(9): 862-868. |
[5] |
YANG Xia,BAI Ying-long,XU Meng,GUO Shi-ju. Effect of Additive Cu-10Sn on Sintering Behavior and Wear Resistance of 316L Stainless Steel[J]. Chinese Journal of Iron and Steel, 2013, 20(7): 84-88. |
[6] |
S Narayan,A Rajeshkannan. Workability Studies in Forming of Sintered Fe-035C Powder Metallurgy Preform During Cold Upsetting[J]. Chinese Journal of Iron and Steel, 2011, 18(12): 71-78. |
|
|
|
|