| Microstructure evolution and corrosion behavior of Nb-alloyed cast heat-resistant steel during different aging treatments |
| Lv‑dan Teng1, Tian‑tian Zhao1, Teng‑fei Cheng1, Yi‑tao Yang1 |
| 1 School of Materials Science and Engineering, Shanghai University, Shanghai 200444, China |
|
|
|
|
Abstract The microstructure evolution of heat-resistant cast stainless steels aged at 600, 700, 800 and 900 °C for 2 h was investigated by scanning electron microscopy and X-ray diffraction. Potentiodynamic polarization curves were applied to study the effects of Nb addition and aging temperature on corrosion resistance. The results demonstrated that eutectoid decomposition of the ferritic phase (δ→σ+γ2) was observed at 700–900 °C. The content of σ-phase first increased and then decreased in the steels, where the maximum content was obtained at 800 °C, indicating that the highest hardness occurred at 800 °C accordingly. The hardness of Nb-containing steels was significantly higher than that of Nb-free steels. The corrosion resistance of heat-resistant cast steels in various aging temperatures was different due to the formation of σ-phase. Both Cr-rich carbides and σ-phase were harmful to the corrosion resistance, while Cr-rich carbides were the main factor. Nb-containing heat-resistant cast steels exhibited superior corrosion resistance, as Cr-rich carbides were reduced and the corrosion products of Nb-rich slowed down the formation of steady-state pits.
|
|
|
|
|
|
| Cite this article: |
|
Lv‑dan Teng,Tian‑tian Zhao,Teng‑fei Cheng, et al. Microstructure evolution and corrosion behavior of Nb-alloyed cast heat-resistant steel during different aging treatments[J]. Journal of Iron and Steel Research International, 2020, 27(12): 1456-1465.
|
|
|
|
| [1] |
1. Central Iron and Steel Research Institute, Beijing 100081, China；2. Qingdao NCS Testing and. YIN Peng-fei,LI Xiang-yang,LU Wen-ping,HAN Bing,YANG Zhao-hui,ZHANG Bo[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 416-422. |
| [2] |
Ming‑ming Pan, Xiao‑ming Zhang, Yong Chen, Xiang‑bin Su, Peng Chen. Effect of cold rolling and annealing on microstructure and properties of a new resource-saving duplex stainless steel Fe–19Cr–0.6Al–12Mn[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(12): 1420-1432. |
| [3] |
Li‑wei Xu, Hua‑bing Li, Huai‑bei Zheng, Peng‑chong Lu, Hao Feng, Shu‑cai Zhang, Wei‑chao Jiao, Zhou‑hua Jiang 1. Effects of nitrogen content on pitting corrosion resistance of non-magnetic drill collar steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(12): 1466-1475. |
| [4] |
Xiang-yu Xu, Long Tian, Yun Zhou, Ming-yu Sun, Xue-min Wang, Cheng-jia Shang, R.D.K. Misra. Effect of Nb on corrosion behavior of inner bottom plate of cargo oil tankers[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(6): 611-620. |
| [5] |
Shang-lin Lv . Zhong-min Yang . Bin Zhang, . Jie Chen . Ying Chen . Xiao-bin Li. Corrosion passive behaviour duplexstainlesssteelat different rates simulated marine-environmentsolution[J]. , 2018, 25(9): 943-953. |
| [6] |
Xue-ying Li,Chun-hua Fan,Qian-lin Wu,Li-hua Dong,Yan-sheng Yin,*,Chang-jun Wang,Jian-xiong Liang. Effect of solution pH, Cl- concentration and temperature on electrochemical behavior of PH13-8Mo steel in acidic environments[J]. , 2017, 24(12): 1238-1247. |
|
|
|
|
2020, Vol. 27 