| Microstructure and mechanical properties in core of a carburizing 20CrNi2MoV bearing steel subjected to cryogenic treatment |
| Chang-sheng Li1, Bin-zhou Li2, Xin Jin1, Yu Wang1 |
| 1 State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, Liaoning, China; 2 Ansteel Group, Ansteel Beijing Research Institute, Beijing 102211, China |
|
|
|
|
Abstract Microstructure and mechanical properties in core of a carburizing 20CrNi2MoV bearing steel subjected to cryogenic treatment were investigated. Conventional treatment sample was quenched and tempered at 180 °C for 2 h. Cryogenic treatment samples were quenched, cryogenically treated at - 80 and - 196 °C for 4 h, slowly returned to room temperature and thereafter tempered at 180 °C for 2 h, and finally tempered at 180 °C for 2 h. The scanning electron microscope, electron backscattering diffraction, X-ray diffraction and transmission electron microscope were adopted for microstructure characterization. The results show that cryogenic treatment increases the fraction of high-angle grain boundaries and the precipitation of finely dispersed carbides in the matrix, decreases the volume fraction of inter-lath retained austenite, and hence improves the strength and hardness. Compared with the conventional treatment, the hardness, yield strength and ultimate tensile strength of the steel after cryogenic treatment are increased by 11.7%, 12.6% and 18.3%, respectively, while the impact energy is decreased by 9.8%.
|
|
|
|
|
|
| Cite this article: |
|
Chang-sheng Li,Bin-zhou Li,Xin Jin, et al. Microstructure and mechanical properties in core of a carburizing 20CrNi2MoV bearing steel subjected to cryogenic treatment[J]. Journal of Iron and Steel Research International, 2021, 28(03): 360-369.
|
|
|
|
| [1] |
Hyungjin Kim, Sangkyu Lee. Printability and physical properties of iron slag powder composites using material extrusion?based 3D printing[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(1): 111-121. |
| [2] |
Dong-hui Li, Wen-chao He, Xu Zhang, Mao-guo Xiao, Shao-hong Li, Kun-yu Zhao, Mao-sheng Yang. Effects of traditional heat treatment and a novel deep cryogenic treatment on microstructure and mechanical properties of low-carbon high-alloy martensitic bearing steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(03): 370-382. |
| [3] |
Wei‑gang Li, Lu Xie, Yun‑tao Zhao, Zi‑xiang Li, Wen‑bo Wang. Prediction model for mechanical properties of hot-rolled strips by deep learning[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(9): 1045-1053. |
| [4] |
Wei-wei Guo, Xiao-xin Zhang, Ying-xue Chen, Zhi-yuan Hong, Qing-zhi Yan. Homogeneity analysis of Y-bearing 12Cr ferritic/martensitic steel fabricated by vacuum induction melting and casting[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(8): 940-951. |
| [5] |
You-hui Jiang, Shun Yao, Wei Liu, Yun Han, Su-peng Liu, Geng Tian, Ai-min Zhao. Influence of annealing temperatures on microstructure evolution and mechanical properties in a low-carbon steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(8): 981-991. |
| [6] |
Chun‑xu Wang, Yuan‑hang Gao, Yong Li, Shun Han, Shao‑zun Liu, Peng‑jie Zhang. Effects of solid-solution temperature on microstructure and mechanical properties of a novel 2000 MPa grade ultra-high-strength steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(6): 710-718. |
|
|
|
|
2021, Vol. 28 