| Relationship between microstructure and corrosion behavior of highgrade pipeline steel in a low-temperature environment |
| Jia-qiang Jing1, Jie Guo1, Ba Li2, Shu-jun Jia2, Yi Ren3 |
1 School of Oil and Gas Engineering, Southwest Petroleum University, Chengdu 610500, Sichuan, China
2 Department of Structural Steels, Central Iron and Steel Research Institute, Beijing 100081, China
3 State Key Laboratory of Metal Material for Marine Equipment and Application of Iron and Steel Research Institutes of Ansteel Group Corporation, Anshan 114009, Liaoning, China |
|
|
|
|
Abstract The relationship between microstructure and corrosion behavior of high-grade pipeline steel under low-temperature conditions was comparatively investigated by the potentiodynamic polarization and electrochemical impedance spectroscopy test combining with optical micrographs, scanning electron microscopy, transmission electron microscopy and electron back-scattered diffraction. The results showed that, compared with room and high temperature, low temperature could influence the corrosion behavior of high-grade pipeline steel, which means that the corrosion potential and current density decreased and the corrosion resistance increased significantly. Moreover, double layer structures of the interface became thicker and more compact. Under low-temperature environment, acicular ferrite had the martensite/austenite constituents with less amount and smaller size, a higher density of low angle grain boundaries and smaller effective grain sizes compared with granular bainite, which demonstrated higher corrosion resistance.
|
|
Received: 08 March 2020
Published: 25 August 2021
|
|
|
|
| Cite this article: |
|
Jia-qiang Jing,Jie Guo,Ba Li, et al. Relationship between microstructure and corrosion behavior of highgrade pipeline steel in a low-temperature environment[J]. Journal of Iron and Steel Research International, 2021, 28(8): 1037-1046.
|
|
|
|
| [1] |
ZHANG Guocheng，LUO Guoping，CHAI Yifan，WANG Yici，SONG Wei. Effect of basicity on liquid phase formation properties and microstructure of sinter[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2021, 33(7): 584-592. |
| [2] |
LI Xiaoyan，YANG Zuohong，YANG Xinlong，LIU Guoliang，JIANG Jun，WANG Jia. Study on cooling process and microstructure of Q550 highstrength steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2021, 33(7): 642-647. |
| [3] |
YANG Jian, CAI Wen-jing. Effect of magnesium treatment on inclusions and HAZ microstructure and properties of steel plate[J]. Iron and Steel, 2021, 56(7): 13-24. |
| [4] |
ZHANG Zhaohui，XU Kaiqiang，XING Xiangdong，LU Huihui，QUAN Jie. Research progress of influence factors on lowtemperature reduction degradation[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2021, 33(6): 453-460. |
| [5] |
LIU Dan，LUO Deng，TANG Wei，GAO Hailiang. Effect of lamellarizing process on microstructure and mechanical properties of high strength marine engineering steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2021, 33(6): 551-556. |
| [6] |
YANG Yue-biao, LI Zong-qiang, DENG Shen, FAN Lei, LIU Qing-you, ZHAO Zheng-zhi. Low temperature impact toughness controlling for Ti-microalloyed high strength steel[J]. Iron and Steel, 2021, 56(3): 41-50. |
|
|
|
|
2021, Vol. 28 