Strain rate sensitivity of a 1.5 GPa nanotwinned steel |
R.D. Liu1, Y.Z. Li2, L. Lin1, C.P. Huang2, Z.H. Cao2, M.X. Huang2 |
1 Iron and Steel Research Institute, Ansteel Group, Anshan 114021, Liaoning, China; 2 Department of Mechanical Engineering, The University of Hong Kong, Hong Kong 999077, China |
|
|
Abstract Two distinct regimes of strain rate sensitivity on yield strength are found in a high-strength nantwinned steel. The yield strength increases from 1410 to 1776 MPa when the strain rate increases from 10–3 to 1400 s-1. It is proposed from the measured small activation volume that the yielding of the nanotwinned steel at higher strain rates is governed by the dislocation bowing out from the carbon atmosphere. At lower strain rates, however, the yielding is controlled by the continuous re-pinning of dislocations due to the fast diffused carbon atoms, which leads to the relative insensitivity of yield strength to the strain rate.
|
|
|
|
|
Cite this article: |
R.D. Liu,Y.Z. Li,L. Lin, et al. Strain rate sensitivity of a 1.5 GPa nanotwinned steel[J]. Journal of Iron and Steel Research International, 2021, 28(11): 1352-1356.
|
|
|
|
[1] |
Ming-jie Qin, Xi Jin, Min Zhang, Hui-jun Yang, Jun-wei Qiao. Twinning induced remarkable strain hardening in a novel Fe50Mn20Cr20Ni10 medium entropy alloy[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(11): 1463-1470. |
[2] |
Qi‑hang Pang, Mei Xu, Zhen‑li Mi, Juan Cui, Jing Guo. Microstructure evolution of ultra-high-strength twinning-induced plasticity (TWIP) steel under dynamic loading[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(1): 66-75. |
[3] |
J. Chen, Y. Zhang, J.J. Wang, C.M. Liu, S.X. Zhao. Multistage serrated flow behavior of a medium-manganese high-carbon steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(9): 1064-1072. |
[4] |
Joong-ki Hwang. Effect of drawing speed on microstructure distribution and drawability in twinning-induced plasticity steel during wire drawing[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(5): 577-587. |
[5] |
Ting‑dong Ren, Wen Shi, Ren‑dong Liu, Li Lin, Hong‑gang Yang, Lin Li, Babar Shahzad. Effect of dew point on hot-dip galvanizing behavior of a high-manganese TWIP steel for automotive application[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(10): 1200-1211. |
[6] |
Joong-ki Hwang, Sung Jin Kim. Effect of reduction in area per pass on strain distribution and microstructure during caliber rolling in twinning-induced plasticity steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(1): 62-74. |
|
|
|
|