Effect of isothermal temper embrittlement and subsequent hydrogen embrittlement on tensile properties of 2.25Cr–1Mo–0.25V base metal and welded metal |
Zhi-peng Shen1,2, Wei Fu1,2, Ling-rui Kong1,2, Han-han Ma1,2, Xiao-hua He1,2, Xiao-chun Yu1,2, Chang-yu Zhou1,2 |
1 School of Mechanical and Power Engineering, Nanjing Tech University, Nanjing 211816, Jiangsu, China 2 Jiangsu Key Lab of Design and Manufacture of Extreme Pressure Equipment, Nanjing 211816, Jiangsu, China |
|
|
Abstract 2.25Cr–1Mo–0.25V base metal (BM) and welded metal (WM) with different temper embrittlement states were obtained by isothermal temper embrittlement test. The ductile–brittle transition temperature and the carbide size of temper embrittled 2.25Cr–1Mo–0.25V BM and WM increased with the isothermal tempering time. The increase in temper embrittlement time leads to a decrease in yield strength (YS) and ultimate tensile strength (UTS). Hydrogen embrittlement (HE) can decrease the ductility and increase YS and UTS of the material. The hydrogen embrittlement sensitivity and microstructure analysis both show a combined effect of HE and temper embrittlement. The deeper the temper embrittlement, the more sensitive the material to HE. When the hydrogen content in the material is low, the WM is less susceptible to HE due to its welding defects.
|
|
|
|
|
Cite this article: |
Zhi-peng Shen,Wei Fu,Ling-rui Kong, et al. Effect of isothermal temper embrittlement and subsequent hydrogen embrittlement on tensile properties of 2.25Cr–1Mo–0.25V base metal and welded metal[J]. Journal of Iron and Steel Research International, 2021, 28(11): 1426-1438.
|
|
|
|
[1] |
Xin Yang, Wen-jun Ma, Yao-jia Ren, Shi-feng Liu, Yan Wang, Wan-lin Wang, Hui-ping Tang. Subgrain microstructures and tensile properties of 316L stainless steel manufactured by selective laser melting[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(9): 1159-1167. |
[2] |
Fu-xing Yin, Xu-chen Li, Cui-xin Chen, Lin Zhao, Yun Peng, Zhi-ling Tian. Microstructure and mechanical properties of weld metal in laser and gas metal arc hybrid welding of 440-MPa-grade high-strength steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(7): 853-861. |
[3] |
Yu‑lu Li, Yue Zhao, Lin Shen, Hao Wu, He‑guo Zhu. Microstructure and mechanical properties of in situ (TiC + SiC)/FeCrCoNi high entropy alloy matrix composites[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(4): 496-504. |
[4] |
Xiao-bing Li, Xin Dong, Peng-xiang Zhao, Wei-wei Xing, Lei-lei Ding, Nan-nan Zhang, Ying-che Ma, Kui Liu. Effect of Mg addition on temper embrittlement in 2.25Cr–1Mo steel doped with 0.056% P–Mg segregation behavior at grain boundary[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(10): 1259-1267. |
[5] |
Maribel Leticia Saucedo-Mun˜oz. Precipitation kinetics of carbides during cyclical and isothermal aging of 2.25Cr–1Mo steel and its effect on mechanical properties[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(10): 1282-1290. |
[6] |
Hyungjin Kim, Sangkyu Lee. Printability and physical properties of iron slag powder composites using material extrusion?based 3D printing[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(1): 111-121. |
|
|
|
|